IS 1570 (Part 5) X85Cr18Mo2V vs EN 10088-1 1.4401

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X85Cr18Mo2V (IS 1570 (Part 5):1985) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X85Cr18Mo2V is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X85Cr18Mo2V vs EN 10088-1 1.4401 is a 59.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X85Cr18Mo2V:
GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
59.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X85Cr18Mo2V EN 10088-1 1.4401
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.80-0.90 ≤0.07
Si (%) <=1.0 ≤1.00
Mn (%) <=1.5 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.035 Not specified
Cr (%) 16.5-18.5 16.5–18.5
Mo (%) <=2.5 2.0–2.5
V (%) <=0.60 Not specified
Ni (%) Not specified 10.5–13.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X85Cr18Mo2V EN 10088-1 1.4401
Hardness 255-306 HB ≤215 HB
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥210 MPa
Elongation Not specified ≥40%
Typical Applications
IS 1570 (Part 5) X85Cr18Mo2V
Not documented
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can IS 1570 (Part 5) X85Cr18Mo2V Be Substituted With EN 10088-1 1.4401?
IS 1570 (Part 5) X85Cr18Mo2V and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X85Cr18Mo2V
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X85Cr18Mo2V
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X85Cr18Mo2V and EN 10088-1 1.4401?
IS 1570 (Part 5) X85Cr18Mo2V specifies P, S, V which are not specified for EN 10088-1 1.4401. EN 10088-1 1.4401 specifies Ni which is not specified for IS 1570 (Part 5) X85Cr18Mo2V.
Can IS 1570 (Part 5) X85Cr18Mo2V be substituted with EN 10088-1 1.4401?
IS 1570 (Part 5) X85Cr18Mo2V and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.