IS 1570 (Part 5) X85Cr18Mo2V vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X85Cr18Mo2V (IS 1570 (Part 5):1985) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X85Cr18Mo2V is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 1570 (Part 5) X85Cr18Mo2V vs GB/T 3280 06Cr19Ni10 is a 61.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X85Cr18Mo2V:
GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
61.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X85Cr18Mo2V GB/T 3280 06Cr19Ni10
Standard IS 1570 (Part 5):1985 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) 0.80-0.90 0.08 max
Si (%) <=1.0 1.00 max
Mn (%) <=1.5 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.035 0.030 max
Cr (%) 16.5-18.5 18.00-20.00
Mo (%) <=2.5 Not specified
V (%) <=0.60 Not specified
Ni (%) Not specified 8.00-11.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X85Cr18Mo2V GB/T 3280 06Cr19Ni10
Hardness 255-306 HB 187 HB max
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified 520-720 MPa
Yield Strength Not specified 205-310 MPa
Elongation Not specified 40-60%
Typical Applications
IS 1570 (Part 5) X85Cr18Mo2V
Not documented
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can IS 1570 (Part 5) X85Cr18Mo2V Be Substituted With GB/T 3280 06Cr19Ni10?
IS 1570 (Part 5) X85Cr18Mo2V and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X85Cr18Mo2V
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
IS 1570 (Part 5) X85Cr18Mo2V
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X85Cr18Mo2V and GB/T 3280 06Cr19Ni10?
IS 1570 (Part 5) X85Cr18Mo2V specifies Mo, V which are not specified for GB/T 3280 06Cr19Ni10. GB/T 3280 06Cr19Ni10 specifies Ni which is not specified for IS 1570 (Part 5) X85Cr18Mo2V.
Can IS 1570 (Part 5) X85Cr18Mo2V be substituted with GB/T 3280 06Cr19Ni10?
IS 1570 (Part 5) X85Cr18Mo2V and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.