IS 1570 (Part 6) XT55W14Cr3V4 vs ASTM A681 H22

Close Alternative — 71.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) XT55W14Cr3V4 (IS 1570 (Part 6):1996) and ASTM A681 H22 (ASTM A681:2008) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) XT55W14Cr3V4 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A681 H22 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 6) XT55W14Cr3V4 vs ASTM A681 H22 is a 71.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 71.7%.

Frequently Compared With IS 1570 (Part 6) XT55W14Cr3V4:
EN ISO 4957 1.2316 GOST 5950 3H2W8F EN ISO 683-17 100Cr6 GB/T 1299 3Cr2W8V DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 GOST 5950 4H5MFS1 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 GB/T 1299 4Cr5MoSiV1 GB/T 1299 4Cr5MoSiV
Match Breakdown
CHEMISTRY MATCH
71.7%
MECHANICAL MATCH
No shared data
OVERALL
71.7%
Specifications
Property IS 1570 (Part 6) XT55W14Cr3V4 ASTM A681 H22
Standard IS 1570 (Part 6):1996 ASTM A681:2008
Category Tool & Die Steels Tool & Die Steels
C (%) 0.50-0.60 0.30-0.40
Si (%) 0.10-0.35 0.15-0.40
Mn (%) 0.20-0.40 0.15-0.40
Cr (%) 2.80-3.30 1.75-3.75
V (%) 0.30-0.60 0.25-0.50
W (%) 13.0-15.0 10.00-11.75
P (%) <=0.035 <=0.030
S (%) <=0.035 <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) XT55W14Cr3V4 ASTM A681 H22
Hardness Not specified <=235 HB
Condition Not specified Annealed (maximum Brinell hardness)
Typical Applications
IS 1570 (Part 6) XT55W14Cr3V4
Not documented
ASTM A681 H22
Tools, dies and fixtures (clause 1.2)
Can IS 1570 (Part 6) XT55W14Cr3V4 Be Substituted With ASTM A681 H22?
IS 1570 (Part 6) XT55W14Cr3V4 and ASTM A681 H22 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 6) XT55W14Cr3V4
0 active listings and RFQs →
ASTM A681 H22
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) XT55W14Cr3V4 and ASTM A681 H22?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 6) XT55W14Cr3V4 be substituted with ASTM A681 H22?
IS 1570 (Part 6) XT55W14Cr3V4 and ASTM A681 H22 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.