IS 1570 (Part 7) 11Cr17Ni13W3TiH vs EN 10088-1 X8CrNiNb16-13

Close Alternative — 70.1% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) and EN 10088-1 X8CrNiNb16-13 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X8CrNiNb16-13 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 7) 11Cr17Ni13W3TiH vs EN 10088-1 X8CrNiNb16-13 is a 70.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.1%.

Frequently Compared With IS 1570 (Part 7) 11Cr17Ni13W3TiH:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 IS 1570 (Part 7) 20Cr12MoNiVH GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
70.1%
MECHANICAL MATCH
No shared data
OVERALL
70.1%
Specifications
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 X8CrNiNb16-13
Standard IS 1570 (Part 7):1992 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 0.04-0.10
Si (%) <=1.00 0.30-0.60
Mn (%) <=1.00 <=1.50
P (%) <=0.045 <=0.035
S (%) <=0.030 <=0.015
Cr (%) 15.5-17.50 15.0-17.0
Ni (%) 12.00-14.50 12.0-14.0
W (%) 2.5-3.5 Not specified
Ti (%) >=4xC, <=0.80 Not specified
B (%) <=0.0006 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 X8CrNiNb16-13
Tensile Strength 600-800 MPa Not specified
Yield Strength >=390 MPa (0.2 % proof stress) Not specified
Elongation >=25% Not specified
Condition Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
EN 10088-1 X8CrNiNb16-13
Not documented
Key Differences
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH Be Substituted With EN 10088-1 X8CrNiNb16-13?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and EN 10088-1 X8CrNiNb16-13 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
EN 10088-1 X8CrNiNb16-13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 11Cr17Ni13W3TiH and EN 10088-1 X8CrNiNb16-13?
IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for EN 10088-1 X8CrNiNb16-13.
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH be substituted with EN 10088-1 X8CrNiNb16-13?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and EN 10088-1 X8CrNiNb16-13 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.