IS 1570 (Part 7) 11Cr17Ni13W3TiH vs IS 1570 (Part 5) X15Cr16Ni2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) and IS 1570 (Part 5) X15Cr16Ni2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 5) X15Cr16Ni2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 7) 11Cr17Ni13W3TiH vs IS 1570 (Part 5) X15Cr16Ni2 is a 72.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 7) 11Cr17Ni13W3TiH:
EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- EN 10088-1 1.4301 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 IS 1570 (Part 7) 20Cr12MoNiVH
Match Breakdown
CHEMISTRY MATCH
72.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 5) X15Cr16Ni2
Standard IS 1570 (Part 7):1992 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 0.10-0.20
Si (%) <=1.00 <=1.0
Mn (%) <=1.00 <=1.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 15.5-17.50 15.0-17.0
Ni (%) 12.00-14.50 1.25-2.50
W (%) 2.5-3.5 Not specified
Ti (%) >=4xC, <=0.80 Not specified
B (%) <=0.0006 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 5) X15Cr16Ni2
Tensile Strength 600-800 MPa Not specified
Yield Strength >=390 MPa (0.2 % proof stress) Not specified
Elongation >=25% Not specified
Condition Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Hardness Not specified <=285 HB
Typical Applications
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
IS 1570 (Part 5) X15Cr16Ni2
Not documented
Key Differences
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH Be Substituted With IS 1570 (Part 5) X15Cr16Ni2?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and IS 1570 (Part 5) X15Cr16Ni2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
IS 1570 (Part 5) X15Cr16Ni2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 11Cr17Ni13W3TiH and IS 1570 (Part 5) X15Cr16Ni2?
IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for IS 1570 (Part 5) X15Cr16Ni2.
Can IS 1570 (Part 7) 11Cr17Ni13W3TiH be substituted with IS 1570 (Part 5) X15Cr16Ni2?
IS 1570 (Part 7) 11Cr17Ni13W3TiH and IS 1570 (Part 5) X15Cr16Ni2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.