IS 1570 (Part 7) 3Cr17Ni12Mo3H vs ASTM A959 316L

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 3Cr17Ni12Mo3H (IS 1570 (Part 7):1992) and ASTM A959 316L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 3Cr17Ni12Mo3H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while ASTM A959 316L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 1570 (Part 7) 3Cr17Ni12Mo3H is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 316L is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 7) 3Cr17Ni12Mo3H vs ASTM A959 316L is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 1570 (Part 7) 3Cr17Ni12Mo3H:
ASTM A959 29-4C ASTM A959 26-3-3 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 1570 (Part 7) 3Cr17Ni12Mo3H ASTM A959 316L
Standard IS 1570 (Part 7):1992 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.00-18.00 16.0-18.0
Ni (%) 10.00-14.00 10.0-14.0
Mo (%) 2.00-3.00 2.00-3.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 3Cr17Ni12Mo3H ASTM A959 316L
Tensile Strength 490-690 MPa Not specified
Yield Strength >=185 MPa (0.2 % proof stress) Not specified
Elongation >=30% Not specified
Condition Tubes, plates, Q, thickness - (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 3Cr17Ni12Mo3H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
ASTM A959 316L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 1570 (Part 7) 3Cr17Ni12Mo3H Be Substituted With ASTM A959 316L?
IS 1570 (Part 7) 3Cr17Ni12Mo3H and ASTM A959 316L overlap closely enough on chemistry and mechanical properties that ASTM A959 316L is often considered as a substitute for IS 1570 (Part 7) 3Cr17Ni12Mo3H in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 7) 3Cr17Ni12Mo3H
0 active listings and RFQs →
ASTM A959 316L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 3Cr17Ni12Mo3H and ASTM A959 316L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 7) 3Cr17Ni12Mo3H be substituted with ASTM A959 316L?
IS 1570 (Part 7) 3Cr17Ni12Mo3H and ASTM A959 316L overlap closely enough on chemistry and mechanical properties that ASTM A959 316L is often considered as a substitute for IS 1570 (Part 7) 3Cr17Ni12Mo3H in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.