IS 1570 (Part 7) 3Cr18Ni11H vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 3Cr18Ni11H (IS 1570 (Part 7):1992) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 3Cr18Ni11H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 1570 (Part 7) 3Cr18Ni11H is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 7) 3Cr18Ni11H vs EN 10088-1 1.4006 is a 62.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 7) 3Cr18Ni11H:
ASTM A959 201L ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
62.9%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 7) 3Cr18Ni11H EN 10088-1 1.4006
Standard IS 1570 (Part 7):1992 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=2.00 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 17.00-19.00 11.5–13.5
Ni (%) 9.00-13.00 ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 3Cr18Ni11H EN 10088-1 1.4006
Tensile Strength 490-690 MPa ≥540 MPa (annealed)
Yield Strength >=175 MPa (0.2 % proof stress) Not specified
Elongation >=30% ≥18%
Condition Tubes, forgings, plates, Q, thickness - (first row of Table 3) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 1570 (Part 7) 3Cr18Ni11H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 1570 (Part 7) 3Cr18Ni11H Be Substituted With EN 10088-1 1.4006?
IS 1570 (Part 7) 3Cr18Ni11H and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 3Cr18Ni11H
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 1570 (Part 7) 3Cr18Ni11H
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 3Cr18Ni11H and EN 10088-1 1.4006?
IS 1570 (Part 7) 3Cr18Ni11H specifies P, S which are not specified for EN 10088-1 1.4006.
Can IS 1570 (Part 7) 3Cr18Ni11H be substituted with EN 10088-1 1.4006?
IS 1570 (Part 7) 3Cr18Ni11H and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.