IS 1570 (Part 7) 3Cr18Ni11H vs IS 1570 (Part 7) 11Cr17Ni13W3TiH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 3Cr18Ni11H (IS 1570 (Part 7):1992) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 3Cr18Ni11H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) 3Cr18Ni11H is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 7) 3Cr18Ni11H vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 63.9% match. As per mechanical properties, the match is 9.7%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 7) 3Cr18Ni11H:
ASTM A959 201L ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
63.9%
MECHANICAL MATCH
9.7%
OVERALL
35%
Specifications
Property IS 1570 (Part 7) 3Cr18Ni11H IS 1570 (Part 7) 11Cr17Ni13W3TiH
Standard IS 1570 (Part 7):1992 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.07-0.15
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=1.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 17.00-19.00 15.5-17.50
Ni (%) 9.00-13.00 12.00-14.50
W (%) Not specified 2.5-3.5
Ti (%) Not specified >=4xC, <=0.80
B (%) Not specified <=0.0006
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 3Cr18Ni11H IS 1570 (Part 7) 11Cr17Ni13W3TiH
Tensile Strength 490-690 MPa 600-800 MPa
Yield Strength >=175 MPa (0.2 % proof stress) >=390 MPa (0.2 % proof stress)
Elongation >=30% >=25%
Condition Tubes, forgings, plates, Q, thickness - (first row of Table 3) Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Typical Applications
IS 1570 (Part 7) 3Cr18Ni11H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 1570 (Part 7) 3Cr18Ni11H Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 1570 (Part 7) 3Cr18Ni11H and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 3Cr18Ni11H
0 active listings and RFQs →
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 3Cr18Ni11H and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, Ti, B which are not specified for IS 1570 (Part 7) 3Cr18Ni11H.
Can IS 1570 (Part 7) 3Cr18Ni11H be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
IS 1570 (Part 7) 3Cr18Ni11H and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.