Minimal Match — 45.3% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 7) 3Cr18Ni11H (IS 1570 (Part 7):1992) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 1570 (Part 7) 3Cr18Ni11H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
IS 1570 (Part 7) 3Cr18Ni11H is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 1570 (Part 7) 3Cr18Ni11H vs EN 10088-1 1.4845 is a 67.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 45.3%.
Frequently Compared With IS 1570 (Part 7) 3Cr18Ni11H:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 7) 3Cr18Ni11H
EN 10088-1 1.4845
Tensile Strength
490-690 MPa
≥515 MPa
Yield Strength
>=175 MPa (0.2 % proof stress)
≥205 MPa
Elongation
>=30%
≥40%
Condition
Tubes, forgings, plates, Q, thickness - (first row of Table 3)
Not specified
Max Service Temp
Not specified
1100°C continuous
Typical Applications
IS 1570 (Part 7) 3Cr18Ni11H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
IS 1570 (Part 7) 3Cr18Ni11H specifies P, S which are not specified for EN 10088-1 1.4845.
Can IS 1570 (Part 7) 3Cr18Ni11H Be Substituted With EN 10088-1 1.4845?
IS 1570 (Part 7) 3Cr18Ni11H and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 1570 (Part 7) 3Cr18Ni11H and EN 10088-1 1.4845?
IS 1570 (Part 7) 3Cr18Ni11H specifies P, S which are not specified for EN 10088-1 1.4845.
Can IS 1570 (Part 7) 3Cr18Ni11H be substituted with EN 10088-1 1.4845?
IS 1570 (Part 7) 3Cr18Ni11H and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.