Post Stock Login Register

IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH vs ASTM A959 622

Related Material — 65.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH (IS 1570 (Part 7):1992) and ASTM A959 622 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while ASTM A959 622 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 622 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH vs ASTM A959 622 is a 65.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.4%.

Frequently Compared With IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH:
IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
65.4%
MECHANICAL MATCH
No shared data
OVERALL
65.4%
Specifications
Property IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH ASTM A959 622
Standard IS 1570 (Part 7):1992 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.03-0.08 <=0.08
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=1.50
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 13.5-16.00 12.0-15.0
Ni (%) 24.00-27.00 24.0-28.0
Mo (%) 1.00-1.50 2.5-3.5
V (%) 0.10-0.50 Not specified
Ti (%) 1.9-2.30 1.55-2.00
Al (%) <=0.35 <=0.35
B (%) 0.003-0.010 0.001-0.010
Cu (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH ASTM A959 622
Tensile Strength 900-1100 MPa Not specified
Yield Strength >=600 MPa (0.2 % proof stress) Not specified
Elongation >=15% Not specified
Condition Bars, forgings, pipes, plates, S+P, thickness over 5 to 250 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
ASTM A959 622
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH Be Substituted With ASTM A959 622?
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH and ASTM A959 622 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH
0 active listings and RFQs →
ASTM A959 622
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH and ASTM A959 622?
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH specifies V which is not specified for ASTM A959 622. ASTM A959 622 specifies Cu which is not specified for IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH.
Can IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH be substituted with ASTM A959 622?
IS 1570 (Part 7) 6Ni25Cr15Ti2MoVBH and ASTM A959 622 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.