IS 1570 (Part 7) 7Cr19Ni11TiH vs ASTM A959 347H

Strong Match — 87.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 7Cr19Ni11TiH (IS 1570 (Part 7):1992) and ASTM A959 347H (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 7Cr19Ni11TiH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while ASTM A959 347H is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 1570 (Part 7) 7Cr19Ni11TiH is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 347H is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 7) 7Cr19Ni11TiH vs ASTM A959 347H is a 87.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.8%.

Frequently Compared With IS 1570 (Part 7) 7Cr19Ni11TiH:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
87.8%
MECHANICAL MATCH
No shared data
OVERALL
87.8%
Specifications
Property IS 1570 (Part 7) 7Cr19Ni11TiH ASTM A959 347H
Standard IS 1570 (Part 7):1992 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.04-0.10 0.04-0.10
Si (%) 0.20-0.80 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 17.00-20.00 17.0-19.0
Ni (%) 9.00-13.00 9.0-12.0
Ti (%) <=0.60 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 7Cr19Ni11TiH ASTM A959 347H
Tensile Strength 490-690 MPa Not specified
Yield Strength >=155 MPa (0.2 % proof stress) Not specified
Elongation >=30% Not specified
Condition Pipes, bars, forgings, Q1, thickness - (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 7Cr19Ni11TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
ASTM A959 347H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 7) 7Cr19Ni11TiH Be Substituted With ASTM A959 347H?
IS 1570 (Part 7) 7Cr19Ni11TiH and ASTM A959 347H overlap closely enough on chemistry and mechanical properties that ASTM A959 347H is often considered as a substitute for IS 1570 (Part 7) 7Cr19Ni11TiH in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 7) 7Cr19Ni11TiH
0 active listings and RFQs →
ASTM A959 347H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 7Cr19Ni11TiH and ASTM A959 347H?
IS 1570 (Part 7) 7Cr19Ni11TiH specifies Ti which is not specified for ASTM A959 347H.
Can IS 1570 (Part 7) 7Cr19Ni11TiH be substituted with ASTM A959 347H?
IS 1570 (Part 7) 7Cr19Ni11TiH and ASTM A959 347H overlap closely enough on chemistry and mechanical properties that ASTM A959 347H is often considered as a substitute for IS 1570 (Part 7) 7Cr19Ni11TiH in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.