IS 2062 (Part 1) E235B0 vs AS/NZS 3679.1 300

Related Material — 64.3% match based on chemical composition and mechanical property overlap.

IS 2062 (Part 1) E235B0 (IS 2062 (Part 1):2025) and AS/NZS 3679.1 300 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. IS 2062 (Part 1) E235B0 is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while AS/NZS 3679.1 300 is commonly used for hot-rolled structural bars and sections for general structural framing. IS 2062 (Part 1) E235B0 is defined under Bureau of Indian Standards (IS), originating from India, while AS/NZS 3679.1 300 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, IS 2062 (Part 1) E235B0 vs AS/NZS 3679.1 300 is a 96.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 64.3%.

Frequently Compared With IS 2062 (Part 1) E235B0:
IS 2062 (Part 1) E235BR IS 2062 (Part 1) E235C IS 2062 (Part 1) E235A CSA G40.21 400A CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400W ASTM A1008 SS Grade 50 CSA G40.21 260W CSA G40.21 480W GOST 19281 09G2S
Match Breakdown
CHEMISTRY MATCH
96.4%
MECHANICAL MATCH
0%
OVERALL
64.3%
Specifications
Property IS 2062 (Part 1) E235B0 AS/NZS 3679.1 300
Standard IS 2062 (Part 1):2025 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.22
Mn (%) <=1.40 <=1.70
Si (%) <=0.40 <=0.50
S (%) <=0.045 <=0.040
P (%) <=0.045 <=0.040
CEV (%) <=0.39 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 (Part 1) E235B0 AS/NZS 3679.1 300
Tensile Strength >=360 MPa 440-600 MPa
Yield Strength 235 MPa (<=16mm) / 225 MPa (16-40mm) / 215 MPa (40-100mm) / 195 MPa (>100mm) 300 MPa min
Elongation >=26% (<=40mm) / >=25% (40-63mm) / >=24% (63-100mm) / >=22% (>100mm) 22% min
Impact Energy >=27 J at 0°C Not specified
Typical Applications
IS 2062 (Part 1) E235B0
Structural work: welded, bolted and riveted structures and general engineering purposes
AS/NZS 3679.1 300
Hot-rolled structural bars and sections for general structural framing
Key Differences
Can IS 2062 (Part 1) E235B0 Be Substituted With AS/NZS 3679.1 300?
IS 2062 (Part 1) E235B0 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 2062 (Part 1) E235B0
No active listings currently.
AS/NZS 3679.1 300
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2700–2700 mm (106.3–106.3 in)
On M-EX Right Now
IS 2062 (Part 1) E235B0
0 active listings and RFQs →
AS/NZS 3679.1 300
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 (Part 1) E235B0 and AS/NZS 3679.1 300?
IS 2062 (Part 1) E235B0 specifies CEV which is not specified for AS/NZS 3679.1 300.
Can IS 2062 (Part 1) E235B0 be substituted with AS/NZS 3679.1 300?
IS 2062 (Part 1) E235B0 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.