Strong Match — 98.7% match based on chemical composition and mechanical property overlap.

IS 2062 (Part 1) E235B0 (IS 2062 (Part 1):2025) and IS 2062 (Part 1) E235C (IS 2062 (Part 1):2025) are both steel grades. Both fall under the Structural Steel category. IS 2062 (Part 1) E235B0 is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while IS 2062 (Part 1) E235C is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 (Part 1) E235B0 is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 (Part 1) E235C is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 (Part 1) E235B0 vs IS 2062 (Part 1) E235C is a 98.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 98.7%.

Frequently Compared With IS 2062 (Part 1) E235B0:
IS 2062 (Part 1) E235A IS 2062 (Part 1) E235BR CSA G40.21 400A AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 350W CSA G40.21 400W CSA G40.21 260W AS/NZS 3679.1 350 CSA G40.21 480W ASTM A1008 SS Grade 50 GOST 19281 09G2S
Match Breakdown
CHEMISTRY MATCH
98.1%
MECHANICAL MATCH
100%
OVERALL
98.7%
Specifications
Property IS 2062 (Part 1) E235B0 IS 2062 (Part 1) E235C
Standard IS 2062 (Part 1):2025 IS 2062 (Part 1):2025
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.17
Mn (%) <=1.40 <=1.40
Si (%) <=0.40 <=0.40
S (%) <=0.045 <=0.040
P (%) <=0.045 <=0.040
CEV (%) <=0.39 <=0.38
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 (Part 1) E235B0 IS 2062 (Part 1) E235C
Tensile Strength >=360 MPa >=360 MPa
Yield Strength 235 MPa (<=16mm) / 225 MPa (16-40mm) / 215 MPa (40-100mm) / 195 MPa (>100mm) 235 MPa (<=16mm) / 225 MPa (16-40mm) / 215 MPa (40-100mm) / 195 MPa (>100mm)
Elongation >=26% (<=40mm) / >=25% (40-63mm) / >=24% (63-100mm) / >=22% (>100mm) >=26% (<=40mm) / >=25% (40-63mm) / >=24% (63-100mm) / >=22% (>100mm)
Impact Energy >=27 J at 0°C >=27 J at -20°C
Typical Applications
IS 2062 (Part 1) E235B0
Structural work: welded, bolted and riveted structures and general engineering purposes
IS 2062 (Part 1) E235C
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 (Part 1) E235B0 Be Substituted With IS 2062 (Part 1) E235C?
IS 2062 (Part 1) E235B0 and IS 2062 (Part 1) E235C overlap closely enough on chemistry and mechanical properties that IS 2062 (Part 1) E235C is often considered as a substitute for IS 2062 (Part 1) E235B0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 2062 (Part 1) E235B0
0 active listings and RFQs →
IS 2062 (Part 1) E235C
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 (Part 1) E235B0 and IS 2062 (Part 1) E235C?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 (Part 1) E235B0 be substituted with IS 2062 (Part 1) E235C?
IS 2062 (Part 1) E235B0 and IS 2062 (Part 1) E235C overlap closely enough on chemistry and mechanical properties that IS 2062 (Part 1) E235C is often considered as a substitute for IS 2062 (Part 1) E235B0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.