IS 2062 E250B0 vs IS 2062 E250B

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 2062 E250B0 (IS 2062:2011) and IS 2062 E250B (IS 2062:2006) are both steel grades. Both fall under the Structural Steel category. IS 2062 E250B0 is typically used for structural sections, welded structures, bridges, transmission towers, industrial fabrication, engineering structures, while IS 2062 E250B is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 E250B0 is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 E250B is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 E250B0 vs IS 2062 E250B is a 100% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 2062 E250B0:
AS/NZS 3679.1 300 IS 2062 E250A CSA G40.21 350W CSA G40.21 260W CSA G40.21 400W CSA G40.21 480W AS/NZS 3679.1 350 GOST 19281 09G2S CSA G40.21 300W IS 2062 E250B0 IS 2062 E250A IS 2062 E250A
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
100%
OVERALL
100%
Specifications
Property IS 2062 E250B0 IS 2062 E250B
Standard IS 2062:2011 IS 2062:2006
Category Structural Steel Structural Steel
C (%) <=0.22 <=0.22
Mn (%) <=1.50 <=1.50
Si (%) <=0.40 <=0.40
S (%) <=0.045 <=0.045
P (%) <=0.045 <=0.045
CEV (%) <=0.41 <=0.41
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E250B0 IS 2062 E250B
Tensile Strength >=410 MPa >=410 MPa
Yield Strength 250 MPa (<=20mm) / 240 MPa (20-40mm) / 230 MPa (>40mm) 250 MPa (<20mm) / 240 MPa (20-40mm) / 230 MPa (>40mm)
Elongation >=23% >=23%
Impact Energy >=27 J at 0°C >=27 J at room temperature (25 +/- 2°C)
Typical Applications
IS 2062 E250B0
structural sections, welded structures, bridges, transmission towers, industrial fabrication, engineering structures
IS 2062 E250B
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 E250B0 Be Substituted With IS 2062 E250B?
IS 2062 E250B0 and IS 2062 E250B overlap closely enough on chemistry and mechanical properties that IS 2062 E250B is often considered as a substitute for IS 2062 E250B0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 2062 E250B0
Angle → (6 listings)
Leg 1: 25–30 mm (0.98–1.18 in)
Leg 2: 20–25 mm (0.79–0.98 in)
Thickness: 3–5 mm (0.12–0.2 in)
IS 2062 E250B
No active listings currently.
On M-EX Right Now
IS 2062 E250B0
6 active listings and RFQs →
IS 2062 E250B
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E250B0 and IS 2062 E250B?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 E250B0 be substituted with IS 2062 E250B?
IS 2062 E250B0 and IS 2062 E250B overlap closely enough on chemistry and mechanical properties that IS 2062 E250B is often considered as a substitute for IS 2062 E250B0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.