IS 2062 E250C vs IS 2062 E250C

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 2062 E250C (IS 2062:2011) and IS 2062 E250C (IS 2062:2006) are both steel grades. Both fall under the Structural Steel category. IS 2062 E250C is typically used for bridges, offshore structures, heavy fabrication, pressure-support structures, industrial structures, crane structures, while IS 2062 E250C is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 E250C is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 E250C is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 E250C vs IS 2062 E250C is a 100% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 2062 E250C:
IS 2062 E250A IS 2062 E250B0 AS/NZS 3679.1 300 CSA G40.21 350W CSA G40.21 400A GOST 19281 09G2S CSA G40.21 400W CSA G40.21 260W CSA G40.21 300W IS 2062 E250B AS/NZS 3679.1 350 IS 2062 E250B0
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
100%
OVERALL
100%
Specifications
Property IS 2062 E250C IS 2062 E250C
Standard IS 2062:2011 IS 2062:2006
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.20
Mn (%) <=1.50 <=1.50
Si (%) <=0.40 <=0.40
S (%) <=0.040 <=0.040
P (%) <=0.040 <=0.040
CEV (%) <=0.39 <=0.39
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E250C IS 2062 E250C
Tensile Strength >=410 MPa >=410 MPa
Yield Strength 250 MPa (<=20mm) / 240 MPa (20-40mm) / 230 MPa (>40mm) 250 MPa (<20mm) / 240 MPa (20-40mm) / 230 MPa (>40mm)
Elongation >=23% >=23%
Impact Energy >=27 J at -20°C >=27 J at room temperature (25 +/- 2°C)
Typical Applications
IS 2062 E250C
bridges, offshore structures, heavy fabrication, pressure-support structures, industrial structures, crane structures
IS 2062 E250C
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 E250C Be Substituted With IS 2062 E250C?
IS 2062 E250C and IS 2062 E250C overlap closely enough on chemistry and mechanical properties that IS 2062 E250C is often considered as a substitute for IS 2062 E250C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 2062 E250C
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2800–3100 mm (110.24–122.05 in)
IS 2062 E250C
No active listings currently.
On M-EX Right Now
IS 2062 E250C
2 active listings and RFQs →
IS 2062 E250C
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E250C and IS 2062 E250C?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 E250C be substituted with IS 2062 E250C?
IS 2062 E250C and IS 2062 E250C overlap closely enough on chemistry and mechanical properties that IS 2062 E250C is often considered as a substitute for IS 2062 E250C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.