IS 4367 37Mn5Si5 vs IS 11169 (Part 1) 10Ni5Cr4

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 4367 37Mn5Si5 (IS 4367:1991) and IS 11169 (Part 1) 10Ni5Cr4 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 4367 37Mn5Si5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 10Ni5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 37Mn5Si5 vs IS 11169 (Part 1) 10Ni5Cr4 is a 58.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 4367 37Mn5Si5:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Mo6H NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
58.9%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 4367 37Mn5Si5 IS 11169 (Part 1) 10Ni5Cr4
Standard IS 4367:1991 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.33-0.41 0.07-0.12
Si (%) 1.10-1.40 <=0.30
Mn (%) 1.10-1.40 0.60-0.90
S (%) <=0.035 <=0.025
P (%) <=0.035 <=0.025
Cr (%) Not specified 0.90-1.20
Cu (%) Not specified <=0.25
Ni (%) Not specified 1.20-1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 37Mn5Si5 IS 11169 (Part 1) 10Ni5Cr4
Tensile Strength 780-930 MPa Not specified
Yield Strength 590 MPa min Not specified
Elongation >=14% Not specified
Hardness (soft annealed) <=217 HB Not specified
Condition Hardened and tempered Not specified
Hardness, ferrite-pearlite (+FP) Not specified 137-187 HB
Tensile Strength, annealed (+AC) Not specified <=520 MPa (over 5 to 40 mm)
Typical Applications
IS 4367 37Mn5Si5
Not documented
IS 11169 (Part 1) 10Ni5Cr4
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can IS 4367 37Mn5Si5 Be Substituted With IS 11169 (Part 1) 10Ni5Cr4?
IS 4367 37Mn5Si5 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 4367 37Mn5Si5
0 active listings and RFQs →
IS 11169 (Part 1) 10Ni5Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 37Mn5Si5 and IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 10Ni5Cr4 specifies Cr, Cu, Ni which are not specified for IS 4367 37Mn5Si5.
Can IS 4367 37Mn5Si5 be substituted with IS 11169 (Part 1) 10Ni5Cr4?
IS 4367 37Mn5Si5 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.