IS 4367 37Mn5Si5 (IS 4367:1991) and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 4367 37Mn5Si5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 4367 37Mn5Si5 vs IS 4367 10Cr9Mo10 is a 55.7% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 4367 37Mn5Si5
IS 4367 10Cr9Mo10
Tensile Strength
780-930 MPa
410-590 MPa
Yield Strength
590 MPa min
245 MPa min
Elongation
>=14%
>=18%
Hardness (soft annealed)
<=217 HB
<=187 HB
Condition
Hardened and tempered
Normalised and tempered, ruling section up to 50 mm
Izod Impact
Not specified
55 J min
Key Differences
IS 4367 10Cr9Mo10 specifies Ni, Cr, Mo which are not specified for IS 4367 37Mn5Si5.
Can IS 4367 37Mn5Si5 Be Substituted With IS 4367 10Cr9Mo10?
IS 4367 37Mn5Si5 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 4367 37Mn5Si5 and IS 4367 10Cr9Mo10?
IS 4367 10Cr9Mo10 specifies Ni, Cr, Mo which are not specified for IS 4367 37Mn5Si5.
Can IS 4367 37Mn5Si5 be substituted with IS 4367 10Cr9Mo10?
IS 4367 37Mn5Si5 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.