IS 5517:1993 40Ni14 Steel: Specifications & Listings
IS 5517:1993 40Ni14: 40Ni14 is a steel in IS 5517:1993 (Steels for Hardening and Tempering), intended in general for forgings and machined parts for engineering or automobile purposes.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
Ni
Cr
S
P
0.35-0.45
0.10-0.35
0.50-0.80
3.20-3.60
<=0.30
<=0.035
<=0.035
Mechanical Properties
Tensile Strength
800-950 MPa
Yield Strength (0.2% proof)
600 MPa min
Elongation
>=16%
Izod Impact
55 J min
Hardness (annealed)
<=229 HB
Condition
Hardened and tempered, ruling section up to 100 mm
More data from IS 5517:1993
From the standard
Heat treatment temperatures5 values
Hot working temperature
1200 to 850 °C
Normalising temperature
830 to 860 °C
Hardening temperature
850 to 860 °C
Quenching medium
Oil
Tempering temperature
550 to 650 °C
Source: IS 5517:1993 with Amendments 1 to 3, Table 4
Properties after hardening and tempering, by ruling section2 sections
Tensile strength (MPa)
0.2% proof stress, min (MPa)
Elongation, min (%)
Izod impact, min (J)
Limiting ruling section (mm)
800 to 950
600
16
55
100
900 to 1050
700
15
55
63
Values apply to test bars taken from rounds along the direction of rolling. Izod impact values are for fine grained steels.
Source: IS 5517:1993 with Amendments 1 to 3, Table 5
Hardness by delivery condition2 conditions
As annealed (A), maximum
229 HB
As rolled (R), maximum
250 HB
Source: IS 5517:1993 with Amendments 1 to 3, Table 6