Strong Match — 98% match
based on chemical composition and mechanical property overlap.
IS 5522 X07Cr18Ni9 (IS 5522:2014) and ASTM A276/A276M S30200 (ASTM A276/A276M:2017) are both steel grades.
Both fall under the Stainless Steel category.
IS 5522 X07Cr18Ni9 is typically used for utensils, while ASTM A276/A276M S30200 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished).
IS 5522 X07Cr18Ni9 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S30200 is defined under ASTM International, originating from United States.
As per chemical composition, IS 5522 X07Cr18Ni9 vs ASTM A276/A276M S30200 is a 96.9% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 98%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 5522 X07Cr18Ni9
ASTM A276/A276M S30200
Tensile Strength
>=515 MPa
>=515 MPa
Yield Strength
>=205 MPa
>=205 MPa
Elongation
>=40%
>=40%
Hardness
<=201 HB
Not specified
Condition
Annealed/softened
Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
IS 5522 X07Cr18Ni9
Utensils
ASTM A276/A276M S30200
Stainless steel bars and shapes (hot-finished or cold-finished)
Can IS 5522 X07Cr18Ni9 Be Substituted With ASTM A276/A276M S30200?
IS 5522 X07Cr18Ni9 and ASTM A276/A276M S30200 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S30200 is often considered as a substitute for IS 5522 X07Cr18Ni9 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 5522 X07Cr18Ni9 and ASTM A276/A276M S30200?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 5522 X07Cr18Ni9 be substituted with ASTM A276/A276M S30200?
IS 5522 X07Cr18Ni9 and ASTM A276/A276M S30200 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S30200 is often considered as a substitute for IS 5522 X07Cr18Ni9 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.