IS 6603 X01Cr24Ni22Mo4CuNW vs ASTM A959 S32654

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 6603 X01Cr24Ni22Mo4CuNW (IS 6603:2024) and ASTM A959 S32654 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X01Cr24Ni22Mo4CuNW is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A959 S32654 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 6603 X01Cr24Ni22Mo4CuNW is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S32654 is defined under ASTM International, originating from United States.

As per chemical composition, IS 6603 X01Cr24Ni22Mo4CuNW vs ASTM A959 S32654 is a 72% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 6603 X01Cr24Ni22Mo4CuNW:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
72%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 6603 X01Cr24Ni22Mo4CuNW ASTM A959 S32654
Standard IS 6603:2024 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.50
Mn (%) 2.0-4.0 2.0-4.0
P (%) <=0.030 <=0.030
S (%) <=0.010 <=0.005
Cr (%) 23.0-25.0 24.0-25.0
Mo (%) 5.5-6.5 7.0-8.0
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.35-0.50 0.45-0.55
Cu (%) 1.00-2.00 0.30-0.60
W (%) 1.50-2.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X01Cr24Ni22Mo4CuNW ASTM A959 S32654
Tensile Strength 800-1000 MPa Not specified
Yield Strength >=420 MPa Not specified
Elongation >=50% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 60 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X01Cr24Ni22Mo4CuNW
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A959 S32654
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 6603 X01Cr24Ni22Mo4CuNW Be Substituted With ASTM A959 S32654?
IS 6603 X01Cr24Ni22Mo4CuNW and ASTM A959 S32654 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 6603 X01Cr24Ni22Mo4CuNW
0 active listings and RFQs →
ASTM A959 S32654
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X01Cr24Ni22Mo4CuNW and ASTM A959 S32654?
IS 6603 X01Cr24Ni22Mo4CuNW specifies W which is not specified for ASTM A959 S32654.
Can IS 6603 X01Cr24Ni22Mo4CuNW be substituted with ASTM A959 S32654?
IS 6603 X01Cr24Ni22Mo4CuNW and ASTM A959 S32654 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.