Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Mo
Ni
N
<=0.020
<=0.25
<=2.00
<=0.025
<=0.010
24.0-26.0
<=0.20
20.0-22.0
<=0.10
Mechanical Properties
Tensile Strength
470-670 MPa
Condition
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, rod only; Yield Strength is Rp0.2, Elongation is A (longitudinal)
More data from IS 6603:2024
From the standard
Mechanical properties by thickness or diameter1 size range
Thickness or diameter (mm)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A min, longitudinal (%)
A min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
rod only
-
-
470 to 670
-
-
-
-
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; elongation and proof strength are not valid for rod.
Source: IS 6603:2024, Table 5
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1030 to 1110 deg C
Cooling after solution annealing
water, air (rapid cooling)
Informative guideline (Annex A).
Source: IS 6603:2024, Table 20