IS 6603:2024 X02Cr24Ni4Mn3Mo2CuN Steel: Specifications & Listings

IS 6603:2024 X02Cr24Ni4Mn3Mo2CuN: X02Cr24Ni4Mn3Mo2CuN: austenitic-ferritic (duplex) corrosion resisting stainless steel, numerical symbol 2441. Specified in IS 6603:2024.

Category: Stainless Steel
Grade Details
GradeIS 6603:2024 X02Cr24Ni4Mn3Mo2CuN
Standard IS 6603:2024
ApplicationsGeneral purposes, semi-finished products, bars, wire rods and bright bars
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-3 X2CrNiMnMoCuN24-4-3-2 EN 10088-3:2014 Europe No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 EN 10088-1:2023 Strong Match
EN 10088-3 X2CrNiMnMoCuN24-4-3-2 EN 10088-3:2014 Strong Match
ASTM A240/A240M S82441 ASTM A240/A240M:2025 Close Alternative
ASTM A276/A276M S82441 ASTM A276/A276M:2017 Close Alternative
ASTM A959 S32950 ASTM A959:2011 Close Alternative
IS 11169 (Part 2) X02Cr17Ni12Mo2 IS 11169 (Part 2):2023 Related Material
IS 11169 (Part 2) X02Cr17Ni12Mo3 IS 11169 (Part 2):2023 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Mo Ni N Cu
<=0.030 <=0.70 2.50-4.0 <=0.035 <=0.005 23.0-25.0 1.00-2.00 3.0-4.5 0.20-0.30 0.10-0.80
Mechanical Properties
Tensile Strength >=650 MPa
Yield Strength >=450 MPa
Elongation >=25%
Hardness <=290 HB
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only

More data from IS 6603:2024

From the standard
Mechanical properties by thickness or diameter 1 size range
Thickness or diameter (mm)Hardness HB (guidance)Rp0.2 min (MPa)Rm min (MPa)A min (%)KV2 min (J)
up to 1602904506502560
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: IS 6603:2024, Table 6
Bright bars, solution annealed 3 rows
Thickness or diameter (mm)Rp0.2 min (MPa)Rm (MPa)A5 min (%)KV2 min (J)
up to 10700900 to 115015-
over 10 to 30700900 to 110020-
over 30 to 160450650 to 9002560
Bright bars, conditions 2H, 2B, 2G or 2P; A5 valid for 5 mm and above.
Source: IS 6603:2024, Table 16
Proof strength at elevated temperature 4 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100385
150345
200325
250315
Minimum values, solution annealed (+AT); for guidance only.
Source: IS 6603:2024, Table 11
Hot forming and solution annealing guideline temperatures
Hot forming temperature
1150 to 900 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1000 to 1150 deg C
Cooling after solution annealing
water, air
Informative guideline (Annex A).
Source: IS 6603:2024, Table 21

Active IS 6603:2024 X02Cr24Ni4Mn3Mo2CuN Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 6603:2024 X02Cr24Ni4Mn3Mo2CuN listings at this time.

Register for Alerts

Buyer RFQs for IS 6603:2024 X02Cr24Ni4Mn3Mo2CuN

+ Post an RFQ for this grade

No open buyer requirements for IS 6603:2024 X02Cr24Ni4Mn3Mo2CuN at this time.

Register for Alerts