IS 6603 X02Cr24Ni4Mn3Mo2CuN vs ASTM A276/A276M S82441

Close Alternative — 79.9% match based on chemical composition and mechanical property overlap.

IS 6603 X02Cr24Ni4Mn3Mo2CuN (IS 6603:2024) and ASTM A276/A276M S82441 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X02Cr24Ni4Mn3Mo2CuN is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while ASTM A276/A276M S82441 is commonly used for stainless steel bars and shapes (hot-finished or cold-finished). IS 6603 X02Cr24Ni4Mn3Mo2CuN is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S82441 is defined under ASTM International, originating from United States.

As per chemical composition, IS 6603 X02Cr24Ni4Mn3Mo2CuN vs ASTM A276/A276M S82441 is a 94.8% match. As per mechanical properties, the match is 50%. Combined, this makes them a close alternative overall at 79.9%.

Frequently Compared With IS 6603 X02Cr24Ni4Mn3Mo2CuN:
EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
94.8%
MECHANICAL MATCH
50%
OVERALL
79.9%
Specifications
Property IS 6603 X02Cr24Ni4Mn3Mo2CuN ASTM A276/A276M S82441
Standard IS 6603:2024 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.70 Not specified
Mn (%) 2.50-4.0 2.5-4.0
P (%) <=0.035 <=0.035
S (%) <=0.005 <=0.005
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 1.00-2.00 1.00-2.00
Ni (%) 3.0-4.5 3.0-4.5
N (%) 0.20-0.30 0.20-0.30
Cu (%) 0.10-0.80 0.10-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X02Cr24Ni4Mn3Mo2CuN ASTM A276/A276M S82441
Tensile Strength >=650 MPa >=740 MPa
Yield Strength >=450 MPa >=540 MPa
Elongation >=25% >=25%
Hardness <=290 HB <=290 HB
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed)
Typical Applications
IS 6603 X02Cr24Ni4Mn3Mo2CuN
General purposes, semi-finished products, bars, wire rods and bright bars
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can IS 6603 X02Cr24Ni4Mn3Mo2CuN Be Substituted With ASTM A276/A276M S82441?
IS 6603 X02Cr24Ni4Mn3Mo2CuN and ASTM A276/A276M S82441 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 6603 X02Cr24Ni4Mn3Mo2CuN
0 active listings and RFQs →
ASTM A276/A276M S82441
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X02Cr24Ni4Mn3Mo2CuN and ASTM A276/A276M S82441?
IS 6603 X02Cr24Ni4Mn3Mo2CuN specifies Si which is not specified for ASTM A276/A276M S82441.
Can IS 6603 X02Cr24Ni4Mn3Mo2CuN be substituted with ASTM A276/A276M S82441?
IS 6603 X02Cr24Ni4Mn3Mo2CuN and ASTM A276/A276M S82441 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.