IS 6603 X04Cr17Ni12Mo2Ti vs EN 10088-1 X6CrNiMoTi17-12-2

Strong Match — 88.9% match based on chemical composition and mechanical property overlap.

IS 6603 X04Cr17Ni12Mo2Ti (IS 6603:2024) and EN 10088-1 X6CrNiMoTi17-12-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X6CrNiMoTi17-12-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 6603 X04Cr17Ni12Mo2Ti vs EN 10088-1 X6CrNiMoTi17-12-2 is a 88.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 88.9%.

Frequently Compared With IS 6603 X04Cr17Ni12Mo2Ti:
EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
88.9%
MECHANICAL MATCH
No shared data
OVERALL
88.9%
Specifications
Property IS 6603 X04Cr17Ni12Mo2Ti EN 10088-1 X6CrNiMoTi17-12-2
Standard IS 6603:2024 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Cr (%) 16.0-18.0 16.5-18.5
Mo (%) 2.00-2.50 2.00-2.50
Ni (%) 10.0-13.5 10.5-13.5
Ti (%) <=0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X04Cr17Ni12Mo2Ti EN 10088-1 X6CrNiMoTi17-12-2
Tensile Strength 520-720 MPa Not specified
Yield Strength >=205 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Not specified
Typical Applications
IS 6603 X04Cr17Ni12Mo2Ti
General purposes, semi-finished products, bars, wire rods and bright bars
EN 10088-1 X6CrNiMoTi17-12-2
Not documented
Key Differences
Can IS 6603 X04Cr17Ni12Mo2Ti Be Substituted With EN 10088-1 X6CrNiMoTi17-12-2?
IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 X6CrNiMoTi17-12-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6CrNiMoTi17-12-2 is often considered as a substitute for IS 6603 X04Cr17Ni12Mo2Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
EN 10088-1 X6CrNiMoTi17-12-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 X6CrNiMoTi17-12-2?
IS 6603 X04Cr17Ni12Mo2Ti specifies Ti which is not specified for EN 10088-1 X6CrNiMoTi17-12-2.
Can IS 6603 X04Cr17Ni12Mo2Ti be substituted with EN 10088-1 X6CrNiMoTi17-12-2?
IS 6603 X04Cr17Ni12Mo2Ti and EN 10088-1 X6CrNiMoTi17-12-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6CrNiMoTi17-12-2 is often considered as a substitute for IS 6603 X04Cr17Ni12Mo2Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.