IS 6603 X04Cr17Ni12Mo2Ti vs IS 6603 X04Cr17Ni12Mo2

Strong Match — 90.4% match based on chemical composition and mechanical property overlap.

IS 6603 X04Cr17Ni12Mo2Ti (IS 6603:2024) and IS 6603 X04Cr17Ni12Mo2 (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. IS 6603 X04Cr17Ni12Mo2Ti is typically used for general purposes, semi-finished products, bars, wire rods and bright bars, while IS 6603 X04Cr17Ni12Mo2 is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars. IS 6603 X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while IS 6603 X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 6603 X04Cr17Ni12Mo2Ti vs IS 6603 X04Cr17Ni12Mo2 is a 85.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 90.4%.

Frequently Compared With IS 6603 X04Cr17Ni12Mo2Ti:
EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
85.6%
MECHANICAL MATCH
100%
OVERALL
90.4%
Specifications
Property IS 6603 X04Cr17Ni12Mo2Ti IS 6603 X04Cr17Ni12Mo2
Standard IS 6603:2024 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.07
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 16.0-18.0
Mo (%) 2.00-2.50 2.00-3.00
Ni (%) 10.0-13.5 10.0-13.0
Ti (%) <=0.80 Not specified
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 6603 X04Cr17Ni12Mo2Ti IS 6603 X04Cr17Ni12Mo2
Tensile Strength 520-720 MPa 520-720 MPa
Yield Strength >=205 MPa >=205 MPa
Elongation >=40% >=40%
Condition Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal) Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
IS 6603 X04Cr17Ni12Mo2Ti
General purposes, semi-finished products, bars, wire rods and bright bars
IS 6603 X04Cr17Ni12Mo2
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can IS 6603 X04Cr17Ni12Mo2Ti Be Substituted With IS 6603 X04Cr17Ni12Mo2?
IS 6603 X04Cr17Ni12Mo2Ti and IS 6603 X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 6603 X04Cr17Ni12Mo2 is often considered as a substitute for IS 6603 X04Cr17Ni12Mo2Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 6603 X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
IS 6603 X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 6603 X04Cr17Ni12Mo2Ti and IS 6603 X04Cr17Ni12Mo2?
IS 6603 X04Cr17Ni12Mo2Ti specifies Ti which is not specified for IS 6603 X04Cr17Ni12Mo2. IS 6603 X04Cr17Ni12Mo2 specifies N which is not specified for IS 6603 X04Cr17Ni12Mo2Ti.
Can IS 6603 X04Cr17Ni12Mo2Ti be substituted with IS 6603 X04Cr17Ni12Mo2?
IS 6603 X04Cr17Ni12Mo2Ti and IS 6603 X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 6603 X04Cr17Ni12Mo2 is often considered as a substitute for IS 6603 X04Cr17Ni12Mo2Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.