JIS G4104 SCr415 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4104 SCr415 (JIS G 4104:1979) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. JIS G4104 SCr415 is typically used for case hardened gears, cams, pins, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. JIS G4104 SCr415 is defined under Japanese Industrial Standards (JIS), originating from Japan, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, JIS G4104 SCr415 vs IS 1570 (Part 7) 10Cr36Mo10H is a 62.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4104 SCr415:
NF A35-565 100C6 UNI 11234 100Cr6 GOST 4543 12HN3A GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
62.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property JIS G4104 SCr415 IS 1570 (Part 7) 10Cr36Mo10H
Standard JIS G 4104:1979 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.13–0.18 <=0.15
Si (%) 0.15–0.35 0.25-1.0
Mn (%) 0.60–0.90 0.30-0.60
Cr (%) 0.90–1.20 8.00-10.00
P (%) ≤0.030 <=0.040
S (%) ≤0.030 <=0.030
Mo (%) Not specified 0.90-1.10
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4104 SCr415 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength ≥735 MPa 410-560 MPa
Case Hardness HRC 56–62 Not specified
Yield Strength Not specified >=135 MPa (0.2 % proof stress)
Elongation Not specified >=20%
Condition Not specified Pipes, A, thickness - (first row of Table 3)
Typical Applications
JIS G4104 SCr415
Case hardened gears, cams, pins
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can JIS G4104 SCr415 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
JIS G4104 SCr415 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4104 SCr415
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5600–5700 mm (220.47–224.41 in)
IS 1570 (Part 7) 10Cr36Mo10H
No active listings currently.
On M-EX Right Now
JIS G4104 SCr415
2 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4104 SCr415 and IS 1570 (Part 7) 10Cr36Mo10H?
IS 1570 (Part 7) 10Cr36Mo10H specifies Mo, Al (metallic) which are not specified for JIS G4104 SCr415.
Can JIS G4104 SCr415 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
JIS G4104 SCr415 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.