JIS G4304 SUS410L vs ASTM A959 S41003

Strong Match — 86.8% match based on chemical composition and mechanical property overlap.

JIS G4304 SUS410L (JIS G4304:2021) and ASTM A959 S41003 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4304 SUS410L is typically used for hot-rolled stainless steel plates and strips, while ASTM A959 S41003 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4304 SUS410L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 S41003 is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4304 SUS410L vs ASTM A959 S41003 is a 86.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.8%.

Frequently Compared With JIS G4304 SUS410L:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
86.8%
MECHANICAL MATCH
No shared data
OVERALL
86.8%
Specifications
Property JIS G4304 SUS410L ASTM A959 S41003
Standard JIS G4304:2021 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.50
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 11.00-13.50 10.5-12.5
Ni (%) <=0.60 <=1.50
N (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4304 SUS410L ASTM A959 S41003
Tensile Strength >=360 MPa Not specified
Yield Strength >=195 MPa Not specified
Elongation >=22% Not specified
Hardness <=183 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4304 SUS410L
Hot-rolled stainless steel plates and strips
ASTM A959 S41003
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4304 SUS410L Be Substituted With ASTM A959 S41003?
JIS G4304 SUS410L and ASTM A959 S41003 overlap closely enough on chemistry and mechanical properties that ASTM A959 S41003 is often considered as a substitute for JIS G4304 SUS410L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
JIS G4304 SUS410L
0 active listings and RFQs →
ASTM A959 S41003
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4304 SUS410L and ASTM A959 S41003?
ASTM A959 S41003 specifies N which is not specified for JIS G4304 SUS410L.
Can JIS G4304 SUS410L be substituted with ASTM A959 S41003?
JIS G4304 SUS410L and ASTM A959 S41003 overlap closely enough on chemistry and mechanical properties that ASTM A959 S41003 is often considered as a substitute for JIS G4304 SUS410L in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.