Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Ni
Al
<=0.08
<=1.00
<=1.00
<=0.040
<=0.030
11.50-14.50
<=0.60
0.10-0.30
Mechanical Properties
Tensile Strength
>=410 MPa
Yield Strength
>=175 MPa
Elongation
>=20%
Hardness
<=183 HB
Condition
Annealed plate and strip; proof strength applies only when specified by the purchaser
More data from JIS G4305:2012
From the standard
Mechanical properties, annealed3 values
0.2 percent proof strength, min
175 MPa
Tensile strength, min
410 MPa
Elongation, min
20 %
0.2 percent proof strength applies only when specified by the purchaser. 1 N/mm2 = 1 MPa.
Source: JIS G 4305:2012, Table 11
Hardness, annealed3 scales
Brinell hardness HBW, max
183
Rockwell HRBW or HRBS, max
88
Vickers hardness HV, max
200
Any one of the hardness scales applies; if not specified the manufacturer selects. HRBW is used in case of dispute.
Source: JIS G 4305:2012, Table 11
Bend test2 values
Bend angle
180 deg
Inside radius
0.5 x thickness for thickness under 8 mm; 1.0 x thickness for thickness 8 mm and over
No cracks on the outside of the test piece.
Source: JIS G 4305:2012, Table 11
Heat treatment (example, informative)1 setting
Annealing
780 to 830 deg C, rapid or slow cooling
Annex JA is informative; temperatures are examples.
Source: JIS G 4305:2012, Table JA.3