JIS G4305 SUS436L vs ASTM A959 29-4C

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS436L (JIS G4305:2012) and ASTM A959 29-4C (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS436L is typically used for cold-rolled stainless steel plates, sheet and strip, while ASTM A959 29-4C is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). JIS G4305 SUS436L is defined under Japanese Industrial Standards (JIS), originating from Japan, while ASTM A959 29-4C is defined under ASTM International, originating from United States.

As per chemical composition, JIS G4305 SUS436L vs ASTM A959 29-4C is a 70.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With JIS G4305 SUS436L:
ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
70.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property JIS G4305 SUS436L ASTM A959 29-4C
Standard JIS G4305:2012 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.025 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 16.00-19.00 28.0-30.0
Mo (%) 0.75-1.50 3.6-4.2
N (%) <=0.025 <=0.045
Ni (%) <=0.60 <=1.00
Ti (%) <=0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS436L ASTM A959 29-4C
Tensile Strength >=410 MPa Not specified
Yield Strength >=245 MPa Not specified
Elongation >=20% Not specified
Hardness <=217 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Not specified
Typical Applications
JIS G4305 SUS436L
Cold-rolled stainless steel plates, sheet and strip
ASTM A959 29-4C
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can JIS G4305 SUS436L Be Substituted With ASTM A959 29-4C?
JIS G4305 SUS436L and ASTM A959 29-4C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4305 SUS436L
0 active listings and RFQs →
ASTM A959 29-4C
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS436L and ASTM A959 29-4C?
JIS G4305 SUS436L specifies Ti which is not specified for ASTM A959 29-4C.
Can JIS G4305 SUS436L be substituted with ASTM A959 29-4C?
JIS G4305 SUS436L and ASTM A959 29-4C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.