JIS G4305 SUS436L vs IS 1570 (Part 7) 11Cr17Ni13W3TiH

Minimal Match — 33.9% match based on chemical composition and mechanical property overlap.

JIS G4305 SUS436L (JIS G4305:2012) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. JIS G4305 SUS436L is typically used for cold-rolled stainless steel plates, sheet and strip, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. JIS G4305 SUS436L is defined under Japanese Industrial Standards (JIS), originating from Japan, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, JIS G4305 SUS436L vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 50.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 33.9%.

Frequently Compared With JIS G4305 SUS436L:
ASTM A959 29-4C ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
50.9%
MECHANICAL MATCH
0%
OVERALL
33.9%
Specifications
Property JIS G4305 SUS436L IS 1570 (Part 7) 11Cr17Ni13W3TiH
Standard JIS G4305:2012 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.025 0.07-0.15
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.00-19.00 15.5-17.50
Mo (%) 0.75-1.50 Not specified
N (%) <=0.025 Not specified
Ni (%) <=0.60 12.00-14.50
Ti (%) <=0.80 >=4xC, <=0.80
W (%) Not specified 2.5-3.5
B (%) Not specified <=0.0006
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4305 SUS436L IS 1570 (Part 7) 11Cr17Ni13W3TiH
Tensile Strength >=410 MPa 600-800 MPa
Yield Strength >=245 MPa >=390 MPa (0.2 % proof stress)
Elongation >=20% >=25%
Hardness <=217 HB Not specified
Condition Annealed plate and strip; proof strength applies only when specified by the purchaser Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Typical Applications
JIS G4305 SUS436L
Cold-rolled stainless steel plates, sheet and strip
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can JIS G4305 SUS436L Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
JIS G4305 SUS436L and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
JIS G4305 SUS436L
0 active listings and RFQs →
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4305 SUS436L and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
JIS G4305 SUS436L specifies Mo, N which are not specified for IS 1570 (Part 7) 11Cr17Ni13W3TiH. IS 1570 (Part 7) 11Cr17Ni13W3TiH specifies W, B which are not specified for JIS G4305 SUS436L.
Can JIS G4305 SUS436L be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
JIS G4305 SUS436L and IS 1570 (Part 7) 11Cr17Ni13W3TiH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.