Post Stock Login Register

KS D3867 SCM435 vs GOST 4543 12HN3A

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

KS D3867 SCM435 (KS D 3867:2025) and GOST 4543 12HN3A (GOST 4543-2016) are both steel grades. Both fall under the Alloy Steel category. KS D3867 SCM435 is typically used for shafts,bolts,studs,axles,gears,structural components,fasteners,machine parts, while GOST 4543 12HN3A is commonly used for used for gears, pinions, crankshafts, aircraft parts, and transmission components.. KS D3867 SCM435 is defined under Korean Industrial Standards (KS) (South Korea).

As per chemical composition, KS D3867 SCM435 vs GOST 4543 12HN3A is a 56.7% match. As per mechanical properties, the match is 13%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With KS D3867 SCM435:
NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 GB/T 3077 12Cr2Ni4A IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Cr36Mo10H EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
56.7%
MECHANICAL MATCH
13%
OVERALL
35%
Specifications
Property KS D3867 SCM435 GOST 4543 12HN3A
Standard KS D 3867:2025 GOST 4543-2016
Category Alloy Steel Alloy Steel
C (%) 0.33-0.38 0.09-0.16
Si (%) 0.15-0.35 0.17-0.37
Mn (%) 0.60-0.85 0.3-0.6
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Cr (%) 0.90-1.20 0.6-0.9
Mo (%) 0.15-0.30 Not specified
Ni (%) Not specified 2.75-3.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property KS D3867 SCM435 GOST 4543 12HN3A
Tensile Strength 930-1080 MPa 850-1050 MPa
Yield Strength 785 MPa min 685 MPa min
Elongation 12-15 % 11% min
Hardness 269-321 HB 58-62 HRC (case)
Typical Applications
KS D3867 SCM435
shafts,bolts,studs,axles,gears,structural components,fasteners,machine parts
GOST 4543 12HN3A
Used for gears, pinions, crankshafts, aircraft parts, and transmission components.
Key Differences
Can KS D3867 SCM435 Be Substituted With GOST 4543 12HN3A?
KS D3867 SCM435 and GOST 4543 12HN3A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
KS D3867 SCM435
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5400–6000 mm (212.6–236.22 in)
GOST 4543 12HN3A
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5600–6600 mm (220.47–259.84 in)
On M-EX Right Now
KS D3867 SCM435
2 active listings and RFQs →
GOST 4543 12HN3A
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between KS D3867 SCM435 and GOST 4543 12HN3A?
KS D3867 SCM435 specifies P, S, Mo which are not specified for GOST 4543 12HN3A. GOST 4543 12HN3A specifies Ni which is not specified for KS D3867 SCM435.
Can KS D3867 SCM435 be substituted with GOST 4543 12HN3A?
KS D3867 SCM435 and GOST 4543 12HN3A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.