Strong Match — 88.8% match
based on chemical composition and mechanical property overlap.
SS 14 22 44 2244 and BS 970 (Part 3) 708M40 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Alloy Steel category.
SS 14 22 44 2244 is typically used for shafts,gears,axles,bolts,forgings,automotive parts,machine components, while BS 970 (Part 3) 708M40 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (table 16).
SS 14 22 44 2244 is defined under Swedish Standards (SS), originating from Sweden, while BS 970 (Part 3) 708M40 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, SS 14 22 44 2244 vs BS 970 (Part 3) 708M40 is a 88.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 88.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (Table 16)
Can SS 14 22 44 2244 Be Substituted With BS 970 (Part 3) 708M40?
SS 14 22 44 2244 and BS 970 (Part 3) 708M40 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 708M40 is often considered as a substitute for SS 14 22 44 2244 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between SS 14 22 44 2244 and BS 970 (Part 3) 708M40?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can SS 14 22 44 2244 be substituted with BS 970 (Part 3) 708M40?
SS 14 22 44 2244 and BS 970 (Part 3) 708M40 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 708M40 is often considered as a substitute for SS 14 22 44 2244 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.