SS 14 22 44 2244 vs UNI 11234 100Cr6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

SS 14 22 44 2244 and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. SS 14 22 44 2244 is typically used for shafts,gears,axles,bolts,forgings,automotive parts,machine components, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. SS 14 22 44 2244 is defined under Swedish Standards (SS), originating from Sweden, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, SS 14 22 44 2244 vs UNI 11234 100Cr6 is a 64.9% match. As per mechanical properties, the match is 19.6%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With SS 14 22 44 2244:
NF A35-565 100C6 GOST 4543 12HN3A GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
64.9%
MECHANICAL MATCH
19.6%
OVERALL
35%
Specifications
Property SS 14 22 44 2244 UNI 11234 100Cr6
Standard SS 14 22 44 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.38-0.45 0.93-1.05
Si (%) <=0.40 0.15-0.35
Mn (%) 0.60-0.90 0.25-0.45
P (%) <=0.025 <=0.025
S (%) <=0.035 <=0.025
Cr (%) 0.90-1.20 1.35-1.65
Mo (%) 0.15-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property SS 14 22 44 2244 UNI 11234 100Cr6
Tensile Strength 900-1100 MPa 750-1000 MPa
Yield Strength 700-900 MPa 400-600 MPa
Elongation 11-16 % 10-14 %
Hardness 248-320 HB 60-64 HRC
Typical Applications
SS 14 22 44 2244
shafts,gears,axles,bolts,forgings,automotive parts,machine components
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can SS 14 22 44 2244 Be Substituted With UNI 11234 100Cr6?
SS 14 22 44 2244 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
SS 14 22 44 2244
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5200–6600 mm (204.72–259.84 in)
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
SS 14 22 44 2244
2 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between SS 14 22 44 2244 and UNI 11234 100Cr6?
SS 14 22 44 2244 specifies Mo which is not specified for UNI 11234 100Cr6.
Can SS 14 22 44 2244 be substituted with UNI 11234 100Cr6?
SS 14 22 44 2244 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.