Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
SS 14 22 44 2244 and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
SS 14 22 44 2244 is defined under Swedish Standards (SS), originating from Sweden, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, SS 14 22 44 2244 vs IS 4367 07Cr4Mo6 is a 61.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
SS 14 22 44 2244
IS 4367 07Cr4Mo6
Tensile Strength
900-1100 MPa
380-550 MPa
Yield Strength
700-900 MPa
225 MPa min
Elongation
11-16 %
>=19%
Hardness
248-320 HB
Not specified
Izod Impact
Not specified
60 J min
Hardness (soft annealed)
Not specified
<=170 HB
Condition
Not specified
Normalised and tempered, ruling section up to 40 mm
IS 4367 07Cr4Mo6 specifies Ni which is not specified for SS 14 22 44 2244.
Can SS 14 22 44 2244 Be Substituted With IS 4367 07Cr4Mo6?
SS 14 22 44 2244 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between SS 14 22 44 2244 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies Ni which is not specified for SS 14 22 44 2244.
Can SS 14 22 44 2244 be substituted with IS 4367 07Cr4Mo6?
SS 14 22 44 2244 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.