AISI 8615 vs IS 11169 (Part 1) 17Ni2Cr2Mo2

Strong Match — 92.2% match based on chemical composition and mechanical property overlap.

AISI 8615 and IS 11169 (Part 1) 17Ni2Cr2Mo2 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. AISI 8615 is typically used for used for gears, shafts, pinions, bushings, transmission parts, and carburized machinery components., while IS 11169 (Part 1) 17Ni2Cr2Mo2 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). AISI 8615 is defined under AISI, originating from United States, while IS 11169 (Part 1) 17Ni2Cr2Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, AISI 8615 vs IS 11169 (Part 1) 17Ni2Cr2Mo2 is a 92.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.2%.

Frequently Compared With AISI 8615:
NF A35-565 100C6 GOST 4543 12HN3A UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5
Match Breakdown
CHEMISTRY MATCH
92.2%
MECHANICAL MATCH
No shared data
OVERALL
92.2%
Specifications
Property AISI 8615 IS 11169 (Part 1) 17Ni2Cr2Mo2
Standard AISI IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.13-0.18 0.15-0.20
Mn (%) 0.70-0.90 0.70-0.90
Si (%) 0.15-0.35 0.15-0.35
Ni (%) 0.40-0.70 0.40-0.70
Cr (%) 0.40-0.60 0.40-0.60
Mo (%) 0.15-0.25 0.15-0.25
P (%) 0.035 max <=0.030
S (%) 0.040 max <=0.040
Cu (%) Not specified <=0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property AISI 8615 IS 11169 (Part 1) 17Ni2Cr2Mo2
Tensile Strength 700-900 MPa Not specified
Yield Strength 500-700 MPa Not specified
Elongation 14-20% Not specified
Hardness 180-240 HB Not specified
Typical Applications
AISI 8615
Used for gears, shafts, pinions, bushings, transmission parts, and carburized machinery components.
IS 11169 (Part 1) 17Ni2Cr2Mo2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can AISI 8615 Be Substituted With IS 11169 (Part 1) 17Ni2Cr2Mo2?
AISI 8615 and IS 11169 (Part 1) 17Ni2Cr2Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 17Ni2Cr2Mo2 is often considered as a substitute for AISI 8615 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
AISI 8615
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4900–6300 mm (192.91–248.03 in)
IS 11169 (Part 1) 17Ni2Cr2Mo2
No active listings currently.
On M-EX Right Now
AISI 8615
2 active listings and RFQs →
IS 11169 (Part 1) 17Ni2Cr2Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between AISI 8615 and IS 11169 (Part 1) 17Ni2Cr2Mo2?
IS 11169 (Part 1) 17Ni2Cr2Mo2 specifies Cu which is not specified for AISI 8615.
Can AISI 8615 be substituted with IS 11169 (Part 1) 17Ni2Cr2Mo2?
AISI 8615 and IS 11169 (Part 1) 17Ni2Cr2Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 17Ni2Cr2Mo2 is often considered as a substitute for AISI 8615 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.