ASTM A276/A276M S31000 vs EN 10088-1 1.4401

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31000 (ASTM A276/A276M:2017) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31000 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment. ASTM A276/A276M S31000 is defined under ASTM International, originating from United States, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S31000 vs EN 10088-1 1.4401 is a 56.2% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S31000:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
56.2%
MECHANICAL MATCH
33.3%
OVERALL
35%
Specifications
Property ASTM A276/A276M S31000 EN 10088-1 1.4401
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.25 ≤0.07
Mn (%) <=2.00 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Si (%) <=1.50 ≤1.00
Cr (%) 24.0-26.0 16.5–18.5
Ni (%) 19.0-22.0 10.5–13.5
Mo (%) Not specified 2.0–2.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31000 EN 10088-1 1.4401
Tensile Strength >=515 MPa ≥520 MPa
Yield Strength >=205 MPa ≥210 MPa
Elongation >=40% ≥40%
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Hardness Not specified ≤215 HB
Typical Applications
ASTM A276/A276M S31000
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can ASTM A276/A276M S31000 Be Substituted With EN 10088-1 1.4401?
ASTM A276/A276M S31000 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S31000
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
ASTM A276/A276M S31000
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31000 and EN 10088-1 1.4401?
ASTM A276/A276M S31000 specifies P, S which are not specified for EN 10088-1 1.4401. EN 10088-1 1.4401 specifies Mo which is not specified for ASTM A276/A276M S31000.
Can ASTM A276/A276M S31000 be substituted with EN 10088-1 1.4401?
ASTM A276/A276M S31000 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.