ASTM A276/A276M S31000 vs GB/T 3280 06Cr19Ni10

Minimal Match — 50.5% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S31000 (ASTM A276/A276M:2017) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S31000 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. ASTM A276/A276M S31000 is defined under ASTM International, originating from United States, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A276/A276M S31000 vs GB/T 3280 06Cr19Ni10 is a 75.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 50.5%.

Frequently Compared With ASTM A276/A276M S31000:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
75.8%
MECHANICAL MATCH
0%
OVERALL
50.5%
Specifications
Property ASTM A276/A276M S31000 GB/T 3280 06Cr19Ni10
Standard ASTM A276/A276M:2017 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.25 0.08 max
Mn (%) <=2.00 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.030 0.030 max
Si (%) <=1.50 1.00 max
Cr (%) 24.0-26.0 18.00-20.00
Ni (%) 19.0-22.0 8.00-11.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S31000 GB/T 3280 06Cr19Ni10
Tensile Strength >=515 MPa 520-720 MPa
Yield Strength >=205 MPa 205-310 MPa
Elongation >=40% 40-60%
Condition Condition A (Annealed), hot-finished, all sizes (first row printed) Not specified
Hardness Not specified 187 HB max
Typical Applications
ASTM A276/A276M S31000
Stainless steel bars and shapes (hot-finished or cold-finished)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Can ASTM A276/A276M S31000 Be Substituted With GB/T 3280 06Cr19Ni10?
ASTM A276/A276M S31000 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S31000
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
ASTM A276/A276M S31000
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S31000 and GB/T 3280 06Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S31000 be substituted with GB/T 3280 06Cr19Ni10?
ASTM A276/A276M S31000 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.