ASTM A276/A276M S32654 vs ASTM A959 S32654

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S32654 (ASTM A276/A276M:2017) and ASTM A959 S32654 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S32654 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while ASTM A959 S32654 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A276/A276M S32654 is defined under ASTM International, originating from United States, while ASTM A959 S32654 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A276/A276M S32654 vs ASTM A959 S32654 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A276/A276M S32654:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A276/A276M S32654 ASTM A959 S32654
Standard ASTM A276/A276M:2017 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Mn (%) 2.0-4.0 2.0-4.0
P (%) <=0.030 <=0.030
S (%) <=0.005 <=0.005
Si (%) <=0.50 <=0.50
Cr (%) 24.0-25.0 24.0-25.0
Ni (%) 21.0-23.0 21.0-23.0
Mo (%) 7.0-8.0 7.0-8.0
N (%) 0.45-0.55 0.45-0.55
Cu (%) 0.30-0.60 0.30-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S32654 ASTM A959 S32654
Tensile Strength >=750 MPa Not specified
Yield Strength >=430 MPa Not specified
Elongation >=40% Not specified
Hardness <=250 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S32654
Stainless steel bars and shapes (hot-finished or cold-finished)
ASTM A959 S32654
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can ASTM A276/A276M S32654 Be Substituted With ASTM A959 S32654?
ASTM A276/A276M S32654 and ASTM A959 S32654 overlap closely enough on chemistry and mechanical properties that ASTM A959 S32654 is often considered as a substitute for ASTM A276/A276M S32654 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A276/A276M S32654
0 active listings and RFQs →
ASTM A959 S32654
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S32654 and ASTM A959 S32654?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A276/A276M S32654 be substituted with ASTM A959 S32654?
ASTM A276/A276M S32654 and ASTM A959 S32654 overlap closely enough on chemistry and mechanical properties that ASTM A959 S32654 is often considered as a substitute for ASTM A276/A276M S32654 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.