ASTM A959 .- vs JIS G4304 SUS430J1L

Strong Match — 85.4% match based on chemical composition and mechanical property overlap.

ASTM A959 .- (ASTM A959:2011) and JIS G4304 SUS430J1L (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 .- is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while JIS G4304 SUS430J1L is commonly used for hot-rolled stainless steel plates and strips. ASTM A959 .- is defined under ASTM International, originating from United States, while JIS G4304 SUS430J1L is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, ASTM A959 .- vs JIS G4304 SUS430J1L is a 85.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.4%.

Frequently Compared With ASTM A959 .-:
ASTM A959 16-8-2H ASTM A959 201L ASTM A959 202 ASTM A959 201 EN 10088-1 1.4301 ASTM A959 201LN ASTM A959 29-4 GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 GOST 5632 08X18H10
Match Breakdown
CHEMISTRY MATCH
85.4%
MECHANICAL MATCH
No shared data
OVERALL
85.4%
Specifications
Property ASTM A959 .- JIS G4304 SUS430J1L
Standard ASTM A959:2011 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.025
Cb (%) 0.10-0.60 Not specified
Cr (%) 18.0-20.0 16.00-20.00
Mn (%) <=1.00 <=1.00
N (%) <=0.030 <=0.025
Ni (%) <=0.50 <=0.60
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Ti (%) 0.07-0.30 <=0.80
Cu (%) Not specified 0.30-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 .- JIS G4304 SUS430J1L
Tensile Strength Not specified >=390 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=22%
Hardness Not specified <=192 HB
Condition Not specified Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
JIS G4304 SUS430J1L
Hot-rolled stainless steel plates and strips
Key Differences
Can ASTM A959 .- Be Substituted With JIS G4304 SUS430J1L?
ASTM A959 .- and JIS G4304 SUS430J1L overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS430J1L is often considered as a substitute for ASTM A959 .- in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 .-
0 active listings and RFQs →
JIS G4304 SUS430J1L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 .- and JIS G4304 SUS430J1L?
ASTM A959 .- specifies Cb which is not specified for JIS G4304 SUS430J1L. JIS G4304 SUS430J1L specifies Cu which is not specified for ASTM A959 .-.
Can ASTM A959 .- be substituted with JIS G4304 SUS430J1L?
ASTM A959 .- and JIS G4304 SUS430J1L overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS430J1L is often considered as a substitute for ASTM A959 .- in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.