Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10025-2 E295 (EN 10025-2:2019) and GOST 19281 09G2S (GOST 19281-2014) are both steel grades.
Both fall under the Structural Steel category.
EN 10025-2 E295 is typically used for hot rolled products of structural steels, while GOST 19281 09G2S is commonly used for used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components..
EN 10025-2 E295 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10025-2 E295 vs GOST 19281 09G2S is a 60.2% match.
As per mechanical properties, the match is 23.5%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10025-2 E295
GOST 19281 09G2S
Tensile Strength
470-610 MPa
490-640 MPa
Yield Strength
>=295 MPa
345 MPa min
Elongation
>=20%
21% min
Condition
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Not specified
Hardness
Not specified
140-190 HB
Typical Applications
EN 10025-2 E295
Hot rolled products of structural steels
GOST 19281 09G2S
Used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.
Key Differences
EN 10025-2 E295 specifies N which is not specified for GOST 19281 09G2S.
GOST 19281 09G2S specifies C, Mn, Si, Ni which are not specified for EN 10025-2 E295.
Can EN 10025-2 E295 Be Substituted With GOST 19281 09G2S?
EN 10025-2 E295 and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10025-2 E295 and GOST 19281 09G2S?
EN 10025-2 E295 specifies N which is not specified for GOST 19281 09G2S. GOST 19281 09G2S specifies C, Mn, Si, Ni which are not specified for EN 10025-2 E295.
Can EN 10025-2 E295 be substituted with GOST 19281 09G2S?
EN 10025-2 E295 and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.