EN 10025-2 E360 vs ASTM A283C

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10025-2 E360 (EN 10025-2:2019) and ASTM A283C (ASTM A283) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 E360 is typically used for hot rolled products of structural steels, while ASTM A283C is commonly used for used for structural fabrication, storage tanks, buildings, bridges, machinery bases, and welded structures.. EN 10025-2 E360 is defined under European Standard (EN), originating from Europe, while ASTM A283C is defined under ASTM International, originating from United States.

As per chemical composition, EN 10025-2 E360 vs ASTM A283C is a 79.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Other Structural Steel Grades to Compare With EN 10025-2 E360:
GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
79.7%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10025-2 E360 ASTM A283C
Standard EN 10025-2:2019 ASTM A283
Category Structural Steel Structural Steel
P (%) <=0.045 0.035 max
S (%) <=0.045 0.040 max
N (%) <=0.012 Not specified
C (%) Not specified 0.24 max
Mn (%) Not specified 0.90 max
Si (%) Not specified 0.40 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 E360 ASTM A283C
Tensile Strength 670-830 MPa 380-515 MPa
Yield Strength >=360 MPa 205 MPa min
Elongation >=11% 23-27%
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Hardness Not specified 120-170 HB
Typical Applications
EN 10025-2 E360
Hot rolled products of structural steels
ASTM A283C
Used for structural fabrication, storage tanks, buildings, bridges, machinery bases, and welded structures.
Key Differences
Can EN 10025-2 E360 Be Substituted With ASTM A283C?
EN 10025-2 E360 and ASTM A283C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 E360
No active listings currently.
ASTM A283C
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3700 mm (114.17–145.67 in)
On M-EX Right Now
EN 10025-2 E360
0 active listings and RFQs →
ASTM A283C
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 E360 and ASTM A283C?
EN 10025-2 E360 specifies N which is not specified for ASTM A283C. ASTM A283C specifies C, Mn, Si which are not specified for EN 10025-2 E360.
Can EN 10025-2 E360 be substituted with ASTM A283C?
EN 10025-2 E360 and ASTM A283C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.