EN 10025-2 S355J0 vs EN 10025-2 S355J2

Strong Match — 97.9% match based on chemical composition and mechanical property overlap.

EN 10025-2 S355J0 (EN 10025-2:2019) and EN 10025-2 S355J2 (EN 10025-2:2019) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S355J0 is typically used for hot rolled products of structural steels, while EN 10025-2 S355J2 is commonly used for used for bridges, offshore structures, cranes, construction equipment, structural frames, and heavy fabrication.. EN 10025-2 S355J0 is defined under European Standard (EN), originating from Europe, while EN 10025-2 S355J2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-2 S355J0 vs EN 10025-2 S355J2 is a 96.9% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 97.9%.

Other Structural Steel Grades to Compare With EN 10025-2 S355J0:
GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A283C
Match Breakdown
CHEMISTRY MATCH
96.9%
MECHANICAL MATCH
100%
OVERALL
97.9%
Specifications
Property EN 10025-2 S355J0 EN 10025-2 S355J2
Standard EN 10025-2:2019 EN 10025-2:2019
Category Structural Steel Structural Steel
C (%) <=0.24 <=0.24
Si (%) <=0.55 <=0.55
Mn (%) <=1.60 <=1.60
P (%) <=0.030 <=0.025
S (%) <=0.030 <=0.025
N (%) <=0.012 Not specified
Cu (%) <=0.55 <=0.55
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S355J0 EN 10025-2 S355J2
Tensile Strength 470-630 MPa 470-630 MPa
Yield Strength >=355 MPa >=355 MPa
Elongation >=22% >=22%
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Applications
EN 10025-2 S355J0
Hot rolled products of structural steels
EN 10025-2 S355J2
Used for bridges, offshore structures, cranes, construction equipment, structural frames, and heavy fabrication.
Key Differences
Can EN 10025-2 S355J0 Be Substituted With EN 10025-2 S355J2?
EN 10025-2 S355J0 and EN 10025-2 S355J2 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S355J2 is often considered as a substitute for EN 10025-2 S355J0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN 10025-2 S355J0
No active listings currently.
EN 10025-2 S355J2
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2800–2800 mm (110.24–110.24 in)
On M-EX Right Now
EN 10025-2 S355J0
0 active listings and RFQs →
EN 10025-2 S355J2
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S355J0 and EN 10025-2 S355J2?
EN 10025-2 S355J0 specifies N which is not specified for EN 10025-2 S355J2.
Can EN 10025-2 S355J0 be substituted with EN 10025-2 S355J2?
EN 10025-2 S355J0 and EN 10025-2 S355J2 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S355J2 is often considered as a substitute for EN 10025-2 S355J0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.