Close Alternative — 74.1% match
based on chemical composition and mechanical property overlap.
EN 10025-2 S500J0 (EN 10025-2:2019) and EN 10025-2 S460K2 (EN 10025-2:2019) are both steel grades.
Both fall under the Structural Steel category.
EN 10025-2 S500J0 is typically used for hot rolled products of structural steels, while EN 10025-2 S460K2 is commonly used for hot rolled products of structural steels.
EN 10025-2 S500J0 is defined under European Standard (EN), originating from Europe, while EN 10025-2 S460K2 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10025-2 S500J0 vs EN 10025-2 S460K2 is a 100% match.
As per mechanical properties, the match is 22.2%.
Combined, this makes them a close alternative overall at 74.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10025-2 S500J0
EN 10025-2 S460K2
Tensile Strength
580-760 MPa
550-720 MPa
Yield Strength
>=500 MPa
>=460 MPa
Elongation
>=15%
>=17%
Condition
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Applications
EN 10025-2 S500J0
Hot rolled products of structural steels
EN 10025-2 S460K2
Hot rolled products of structural steels
Can EN 10025-2 S500J0 Be Substituted With EN 10025-2 S460K2?
EN 10025-2 S500J0 and EN 10025-2 S460K2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10025-2 S500J0 and EN 10025-2 S460K2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10025-2 S500J0 be substituted with EN 10025-2 S460K2?
EN 10025-2 S500J0 and EN 10025-2 S460K2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.