EN 10025-2 S235J0 vs EN 10025-2 S235JR

Strong Match — 99.5% match based on chemical composition and mechanical property overlap.

EN 10025-2 S235J0 (EN 10025-2:2019) and EN 10025-2 S235JR (EN 10025-2:2019) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S235J0 is typically used for used for structural beams, bridges, frames, plates, construction equipment, and welded structures., while EN 10025-2 S235JR is commonly used for structural fabrication, bridges, buildings, general engineering. EN 10025-2 S235J0 is defined under European Standard (EN), originating from Europe, while EN 10025-2 S235JR is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-2 S235J0 vs EN 10025-2 S235JR is a 99.2% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 99.5%.

Frequently Compared With EN 10025-2 S235J0:
CSA G40.21 260W CSA G40.21 400W CSA G40.21 480W CSA G40.21 350W CSA G40.21 300W CSA G40.21 400A AS/NZS 3679.1 300 AS/NZS 3679.1 350 GOST 19281 09G2S ASTM A1008 SS Grade 80 ASTM A283C ASTM A1008 SS Grade 50
Match Breakdown
CHEMISTRY MATCH
99.2%
MECHANICAL MATCH
100%
OVERALL
99.5%
Specifications
Property EN 10025-2 S235J0 EN 10025-2 S235JR
Standard EN 10025-2:2019 EN 10025-2:2019
Category Structural Steel Structural Steel
C (%) <=0.17 <=0.17
Mn (%) <=1.40 <=1.40
P (%) <=0.030 <=0.035
S (%) <=0.030 <=0.035
N (%) <=0.012 <=0.012
Cu (%) <=0.55 <=0.55
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S235J0 EN 10025-2 S235JR
Tensile Strength 360-510 MPa 360-510 MPa
Yield Strength >=235 MPa >=235 MPa
Elongation >=26% >=26%
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Applications
EN 10025-2 S235J0
Used for structural beams, bridges, frames, plates, construction equipment, and welded structures.
EN 10025-2 S235JR
Structural fabrication, bridges, buildings, general engineering
Can EN 10025-2 S235J0 Be Substituted With EN 10025-2 S235JR?
EN 10025-2 S235J0 and EN 10025-2 S235JR overlap closely enough on chemistry and mechanical properties that EN 10025-2 S235JR is often considered as a substitute for EN 10025-2 S235J0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN 10025-2 S235J0
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3900–4400 mm (153.54–173.23 in)
EN 10025-2 S235JR
Plate → (3 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3300–5100 mm (129.92–200.79 in)
On M-EX Right Now
EN 10025-2 S235J0
2 active listings and RFQs →
EN 10025-2 S235JR
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S235J0 and EN 10025-2 S235JR?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10025-2 S235J0 be substituted with EN 10025-2 S235JR?
EN 10025-2 S235J0 and EN 10025-2 S235JR overlap closely enough on chemistry and mechanical properties that EN 10025-2 S235JR is often considered as a substitute for EN 10025-2 S235J0 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.