EN 10025-2 S275 vs EN 10025-2 S275JR

Strong Match — 92% match based on chemical composition and mechanical property overlap.

EN 10025-2 S275 (EN 10025-2:2019) and EN 10025-2 S275JR (EN 10025-2:2019) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S275 is typically used for structural beams, columns, bridges, general fabrication, while EN 10025-2 S275JR is commonly used for general structural work, bridges, machinery frames. EN 10025-2 S275 is defined under European Standard (EN), originating from Europe, while EN 10025-2 S275JR is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-2 S275 vs EN 10025-2 S275JR is a 88% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 92%.

Frequently Compared With EN 10025-2 S275:
CSA G40.21 260W IS 2062 E165 GOST 19281 09G2S CSA G40.21 300W CSA G40.21 400W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A572 Gr.65
Other Structural Steel Grades to Compare With EN 10025-2 S275:
AS/NZS 3679.1 300 AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A
Match Breakdown
CHEMISTRY MATCH
88%
MECHANICAL MATCH
100%
OVERALL
92%
Specifications
Property EN 10025-2 S275 EN 10025-2 S275JR
Standard EN 10025-2:2019 EN 10025-2:2019
Category Structural Steel Structural Steel
C (%) 0-0.25 <=0.21
Mn (%) 0-1.5 <=1.50
Si (%) 0-0.5 Not specified
P (%) max 0.04 <=0.035
S (%) max 0.04 <=0.035
N (%) Not specified <=0.012
Cu (%) Not specified <=0.55
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S275 EN 10025-2 S275JR
Yield Strength 275 MPa min (t<=16mm) >=275 MPa
Tensile Strength 410-560 MPa 410-560 MPa
Elongation 23% min >=23%
Condition Not specified Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Applications
EN 10025-2 S275
Structural beams, columns, bridges, general fabrication
EN 10025-2 S275JR
General structural work, bridges, machinery frames
Key Differences
Can EN 10025-2 S275 Be Substituted With EN 10025-2 S275JR?
EN 10025-2 S275 and EN 10025-2 S275JR overlap closely enough on chemistry and mechanical properties that EN 10025-2 S275JR is often considered as a substitute for EN 10025-2 S275 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN 10025-2 S275
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5000–5000 mm (196.85–196.85 in)
EN 10025-2 S275JR
Plate → (3 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3000–3500 mm (118.11–137.8 in)
On M-EX Right Now
EN 10025-2 S275
2 active listings and RFQs →
EN 10025-2 S275JR
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S275 and EN 10025-2 S275JR?
EN 10025-2 S275 specifies Si which is not specified for EN 10025-2 S275JR. EN 10025-2 S275JR specifies N, Cu which are not specified for EN 10025-2 S275.
Can EN 10025-2 S275 be substituted with EN 10025-2 S275JR?
EN 10025-2 S275 and EN 10025-2 S275JR overlap closely enough on chemistry and mechanical properties that EN 10025-2 S275JR is often considered as a substitute for EN 10025-2 S275 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.