EN 10088-2:2014 X2CrNi12 Steel: Specifications & Listings

EN 10088-2:2014 X2CrNi12: X2CrNi12: ferritic corrosion resisting stainless steel, material number 1.4003. Specified in EN 10088-2:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-2:2014 X2CrNi12
Standard EN 10088-2:2014
ApplicationsGeneral purposes, hot or cold rolled sheet/plate and strip
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S40975 ASTM A959:2011 USA No activity yet
ASTM A959 S40977 ASTM A959:2011 USA No activity yet
ASTM A959 S41050 ASTM A959:2011 USA No activity yet
ASTM A959 S41003 ASTM A959:2011 USA No activity yet
EN 10088-1 X2CrNi12 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrMnNiTi12 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-3 X2CrNi12 EN 10088-3:2014 Europe No activity yet
ASTM A959 S40910 ASTM A959:2011 USA No activity yet
ASTM A959 S40920 ASTM A959:2011 USA No activity yet
ASTM A959 S40930 ASTM A959:2011 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 S40977 ASTM A959:2011 Strong Match
EN 10088-1 X2CrNi12 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNi12 EN 10088-1:2023 Strong Match
ASTM A959 S41003 ASTM A959:2011 Strong Match
EN 10088-1 X2CrMnNiTi12 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrMnNiTi12 EN 10088-1:2023 Strong Match
ASTM A959 S40975 ASTM A959:2011 Strong Match
ASTM A959 S40910 ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Ni N
<=0.030 <=1.00 <=1.50 <=0.040 <=0.015 10.5-12.5 0.30-1.00 <=0.030
Mechanical Properties
Tensile Strength 450-650 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Yield Strength >=280 MPa
Elongation >=20%

More data from EN 10088-2:2014

From the standard
Mechanical properties by product form and thickness 3 product forms
Product formMax thickness (mm)Rp0.2 longitudinal, min (MPa)Rp0.2 transverse, min (MPa)Rm (MPa)A80 min, under 3 mm thick (%)A min, 3 mm and over (%)
Cold rolled strip8280320450 to 6502020
Hot rolled strip13.5280320450 to 6502020
Hot rolled plate25250280450 to 6501818
Annealed condition; one elongation value is printed for both thickness classes.
Source: EN 10088-2:2014, Table 9
Proof strength at elevated temperature 7 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100240
150235
200230
250220
300215
350-
400-
Minimum values, annealed (+A).
Source: EN 10088-2:2014, Table 14
Hot forming and annealing guideline temperatures
Hot forming temperature
1100 to 800 deg C
Cooling after hot forming
air
Heat treatment symbol
+A
Annealing temperature
700 to 760 deg C
Cooling after annealing
air, water
Informative guideline.
Source: EN 10088-2:2014, Table A.3

Active EN 10088-2:2014 X2CrNi12 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-2:2014 X2CrNi12 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-2:2014 X2CrNi12

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-2:2014 X2CrNi12 at this time.

Register for Alerts