EN 10088-3:2014 X2CrNi12 Steel: Specifications & Listings

EN 10088-3:2014 X2CrNi12: X2CrNi12: ferritic corrosion resisting stainless steel, material number 1.4003. Specified in EN 10088-3:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-3:2014 X2CrNi12
Standard EN 10088-3:2014
ApplicationsGeneral purposes, semi-finished products, bars, rods, wire, sections and bright products
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S40975 ASTM A959:2011 USA No activity yet
ASTM A959 S40977 ASTM A959:2011 USA No activity yet
ASTM A959 S41050 ASTM A959:2011 USA No activity yet
ASTM A959 S41003 ASTM A959:2011 USA No activity yet
EN 10088-1 X2CrNi12 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrMnNiTi12 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-2 X2CrNi12 EN 10088-2:2014 Europe No activity yet
ASTM A959 S40910 ASTM A959:2011 USA No activity yet
ASTM A959 S40920 ASTM A959:2011 USA No activity yet
ASTM A959 S40930 ASTM A959:2011 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 S40977 ASTM A959:2011 Strong Match
EN 10088-1 X2CrNi12 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNi12 EN 10088-1:2023 Strong Match
ASTM A959 S41003 ASTM A959:2011 Strong Match
ASTM A959 S40975 ASTM A959:2011 Strong Match
EN 10088-1 X2CrMnNiTi12 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrMnNiTi12 EN 10088-1:2023 Strong Match
ASTM A959 S41050 ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Ni N
<=0.030 <=1.00 <=1.50 <=0.040 <=0.030 10.5-12.5 0.30-1.00 <=0.030
Mechanical Properties
Tensile Strength 450-600 MPa
Yield Strength >=260 MPa
Elongation >=20%
Hardness <=200 HB
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only

More data from EN 10088-3:2014

From the standard
Mechanical properties by thickness or diameter 1 size range
Thickness or diameter, max (mm)Hardness HBW, max (guidance)Rp0.2 min (MPa)Rm (MPa)A min, longitudinal (%)
up to 100200260450 to 60020
Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 10
Proof strength at elevated temperature 7 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100240
150230
200220
250215
300210
350-
400-
Minimum values, annealed (+A).
Source: EN 10088-3:2014, Table 22
Hot forming and annealing guideline temperatures
Hot forming temperature
1100 to 800 deg C
Cooling after hot forming
air
Heat treatment symbol
+A
Annealing temperature
680 to 740 deg C
Cooling after annealing
air
Informative guideline.
Source: EN 10088-3:2014, Table A.3

Active EN 10088-3:2014 X2CrNi12 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-3:2014 X2CrNi12 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-3:2014 X2CrNi12

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-3:2014 X2CrNi12 at this time.

Register for Alerts