GOST 19281 09G2S vs ASTM A959 309

Related Material — 65% match based on chemical composition and mechanical property overlap.

GOST 19281 09G2S (GOST 19281-2014) and ASTM A959 309 (ASTM A959:2011) are both steel grades. GOST 19281 09G2S is classified under Structural Steel, while ASTM A959 309 is classified under Stainless Steel — a different category, which is worth noting alongside the chemistry match below. GOST 19281 09G2S is typically used for used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components., while ASTM A959 309 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 309 is defined under ASTM International (United States).

As per chemical composition, GOST 19281 09G2S vs ASTM A959 309 is a 65.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With GOST 19281 09G2S:
ASTM A1008 SS Grade 50 AS/NZS 1595 C450 IS 2062 E250B0 CSA G40.21 400W CSA G40.21 300W CSA G40.21 480W ASTM A1008 SS Grade 80 CSA G40.21 260W AS/NZS 1595 C350 ASTM A572 Grade 50 IS 2062 E250A CSA G40.21 350W
Match Breakdown
CHEMISTRY MATCH
65.1%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property GOST 19281 09G2S ASTM A959 309
Standard GOST 19281-2014 ASTM A959:2011
Category Structural Steel Stainless Steel
C (%) 0.07-0.12 <=0.20
Mn (%) 1.3-1.7 <=2.00
Si (%) 0.5-0.8 <=1.00
S (%) 0.04 max <=0.030
P (%) 0.035 max <=0.045
Ni (%) 0.3 max 12.0-15.0
Cr (%) 0.3 max 22.0-24.0
Cu (%) 0.3 max Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 19281 09G2S ASTM A959 309
Tensile Strength 490-640 MPa Not specified
Yield Strength 345 MPa min Not specified
Elongation 21% min Not specified
Hardness 140-190 HB Not specified
Typical Applications
GOST 19281 09G2S
Used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.
ASTM A959 309
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can GOST 19281 09G2S Be Substituted With ASTM A959 309?
GOST 19281 09G2S and ASTM A959 309 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 19281 09G2S
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3800 mm (114.17–149.61 in)
ASTM A959 309
No active listings currently.
On M-EX Right Now
GOST 19281 09G2S
2 active listings and RFQs →
ASTM A959 309
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 19281 09G2S and ASTM A959 309?
Different category: GOST 19281 09G2S is Structural Steel, ASTM A959 309 is Stainless Steel. GOST 19281 09G2S specifies Cu which is not specified for ASTM A959 309.
Can GOST 19281 09G2S be substituted with ASTM A959 309?
GOST 19281 09G2S and ASTM A959 309 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.