GOST 19281 09G2S vs EN 10088-1 X12Cr13

Related Material — 65% match based on chemical composition and mechanical property overlap.

GOST 19281 09G2S (GOST 19281-2014) and EN 10088-1 X12Cr13 (EN 10088-1:2014) are both steel grades. GOST 19281 09G2S is classified under Structural Steel, while EN 10088-1 X12Cr13 is classified under Stainless Steel — a different category, which is worth noting alongside the chemistry match below. GOST 19281 09G2S is typically used for used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components., while EN 10088-1 X12Cr13 is commonly used for cutlery, turbine blades, valve parts, fasteners. EN 10088-1 X12Cr13 is defined under European Standard (EN) (Europe).

As per chemical composition, GOST 19281 09G2S vs EN 10088-1 X12Cr13 is a 69.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With GOST 19281 09G2S:
ASTM A1008 SS Grade 50 AS/NZS 1595 C450 IS 2062 E250B0 CSA G40.21 400W CSA G40.21 300W CSA G40.21 480W ASTM A1008 SS Grade 80 CSA G40.21 260W AS/NZS 1595 C350 ASTM A572 Grade 50 IS 2062 E250A CSA G40.21 350W
Match Breakdown
CHEMISTRY MATCH
69.3%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property GOST 19281 09G2S EN 10088-1 X12Cr13
Standard GOST 19281-2014 EN 10088-1:2014
Category Structural Steel Stainless Steel
C (%) 0.07-0.12 0.08-0.15
Mn (%) 1.3-1.7 <=1.50
Si (%) 0.5-0.8 <=1.00
S (%) 0.04 max <=0.015
P (%) 0.035 max <=0.040
Ni (%) 0.3 max <=0.75
Cr (%) 0.3 max 11.5-13.5
Cu (%) 0.3 max Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 19281 09G2S EN 10088-1 X12Cr13
Tensile Strength 490-640 MPa Not specified
Yield Strength 345 MPa min Not specified
Elongation 21% min Not specified
Hardness 140-190 HB Not specified
Typical Applications
GOST 19281 09G2S
Used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.
EN 10088-1 X12Cr13
Cutlery, turbine blades, valve parts, fasteners
Key Differences
Can GOST 19281 09G2S Be Substituted With EN 10088-1 X12Cr13?
GOST 19281 09G2S and EN 10088-1 X12Cr13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 19281 09G2S
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3800 mm (114.17–149.61 in)
EN 10088-1 X12Cr13
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–4000 mm (98.43–157.48 in)
On M-EX Right Now
GOST 19281 09G2S
2 active listings and RFQs →
EN 10088-1 X12Cr13
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 19281 09G2S and EN 10088-1 X12Cr13?
Different category: GOST 19281 09G2S is Structural Steel, EN 10088-1 X12Cr13 is Stainless Steel. GOST 19281 09G2S specifies Cu which is not specified for EN 10088-1 X12Cr13.
Can GOST 19281 09G2S be substituted with EN 10088-1 X12Cr13?
GOST 19281 09G2S and EN 10088-1 X12Cr13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.