GOST 5632 06Kh23N28 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GOST 5632 06Kh23N28 (GOST 5632-2014) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 06Kh23N28 is typically used for furnace components, heat exchangers, high temperature applications, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. EN 10088-1 1.4006 is defined under European Standard (EN) (Europe).

As per chemical composition, GOST 5632 06Kh23N28 vs EN 10088-1 1.4006 is a 75% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GOST 5632 06Kh23N28:
EN 10088-1 1.4845 EN 10088-1 1.4301 EN 10088-1 1.4401 ASTM A959 26-3-3 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 16-8-2H ASTM A959 29-4 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoH ASTM A959 201
Match Breakdown
CHEMISTRY MATCH
75%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property GOST 5632 06Kh23N28 EN 10088-1 1.4006
Standard GOST 5632-2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) ≤0.06 0.08–0.15
Si (%) ≤0.80 ≤1.00
Mn (%) ≤2.00 ≤1.50
Cr (%) 22.0–25.0 11.5–13.5
Ni (%) 26.0–29.0 ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 06Kh23N28 EN 10088-1 1.4006
Tensile Strength ≥510 MPa ≥540 MPa (annealed)
Yield Strength ≥196 MPa Not specified
Elongation ≥35% ≥18%
Max Service Temp 1050°C Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Can GOST 5632 06Kh23N28 Be Substituted With EN 10088-1 1.4006?
GOST 5632 06Kh23N28 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
GOST 5632 06Kh23N28
2 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 06Kh23N28 and EN 10088-1 1.4006?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can GOST 5632 06Kh23N28 be substituted with EN 10088-1 1.4006?
GOST 5632 06Kh23N28 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.